Extrusion Foaming of DCP Slightly Cross-linked High-density Polyethylene by Supercritical CO_2

ZHANG Yuxia,LIU Bengang,CHEN Yun,HE Ludong,WANG Xiangdong,DU Zhongjie
2012-01-01
Abstract:High-density polyethylene(PE-HD) was slightly cross-linked by various contents of dicumyl peroxide(DCP).The melt strength and crystallization behavior of the resultants were characterized by Rheotens and DSC.It was shown that low contents of DCP led to the decrease of melt strength of the resultant,but increased their crystallization rates and crystallization degree;while the contents of DCP was 0.5 phr,the melt strength of the resultant reached its highest value,0.127 N,and lowest crystallization degree.The resultants were extrusion foamed by supercritical CO2,and the resultant foams were observed by SEM and a density meter.The results showed that while the contents of DCP was 0.5 phr,the foam was endowed with the best cell morphology with the smallest cell size and lowest density of 0.5853 g/cm3.