Abstract:Growing global awareness of environmental issues has led to increased research interest in starch-based foams as a biodegradable packaging material. However, limitations such as low foaming ratio and poor water resistance hinder their development and industrial application. This study aimed to address these challenges by investigating the effect of the polyvinyl alcohol (PVA) content and hydrolysis degree on foam properties, providing insight into the intricate interplay between melt viscoelasticity and foam characteristics. The results demonstrated that the foaming behaviors, viscoelastic properties, thermal stabilities and mechanical performances of the foams were significantly improved with increasing hydrolysis degrees of PVA. These enhancements were attributed to hydrogen bonding interactions and intermolecular entanglements between starch and PVA chains. Additionally, the incorporation of PVA resulted in a remarkable reduction in the water absorption capacity (WAC) of the foams. Specifically, the foam containing 20% PVA with a hydrolysis degree of 98% exhibited the lowest WAC of 7.46% at 75% RH, the lowest bulk density of 12.42 kg/m 3 , the highest foaming ratio of 54.66, and the highest porosity of 99.39%. These properties were equivalent to those of commercially available expanded polystyrene (EPS). Furthermore, the addition of 20% PVA yielded the highest compressive strength of 110.58 MPa and the highest recovery of 92.75%, indicating great potential for diverse cushioning applications. Overall, this work highlights the significant potential for wider application of starch-based foams in large-scale industrial settings.

Effect of Plasticizer on the Morphology and Foaming Properties of Poly(vinyl alcohol) Foams by Supercritical CO2 Foaming Agents

Effect of Melt Viscosity on the Cell Morphology and Properties of Poly(lactic Acid) Foams

Effects of Processing Parameters and Thermal History on Microcellular Foaming Behaviors of PEEK Using Supercritical CO2

Tailored Morphologies and Properties of High-Performance Microcellular Poly(phenylene Sulfide)/poly(ether Ether Ketone) (PPS/PEEK) Blends

Study on Microcellular Foaming of Poly(phenylene sulifde)/Poly(ether ether ketone) Blends Using Supercritical Carbon Dioxide

Effects of polyvinyl alcohol content and hydrolysis degree on the structure and properties of extruded starch-based foams

Effect of Boric Acid on the Foaming Properties and Cell Structure of Poly(vinyl alcohol) Foam Prepared by Supercritical-CO2 Thermoplastic Extrusion Foaming

Melt Extrusion Foaming of Modified PVA and Effecting Factor

Biodegradable and Ultra-High Expansion Ratio PPC-P Foams Achieved by Microcellular Foaming Using CO2 as Blowing Agent

Influence of TPU/EVA Phase Morphology Evolution on Supercritical Carbon Dioxide Extrusion Foaming

Microcellular foaming of PP/PE blends with different viscosity and elasticity

Fundamental Influences of Induced Crystallization and Phase Separation on the Foaming Behavior of Poly(Lactic Acid)/Polyethylene Glycol Blends Blown with Compressed Co2

Preparation of Biodegradable PBST/PLA Microcellular Foams under Supercritical CO2: Heterogeneous Nucleation and Anti-Shrinkage Effect of PLA

Reinforcing a Thermoplastic Starch/Poly(butylene adipate-co-terephthalate) Composite Foam with Polyethylene Glycol under Supercritical Carbon Dioxide

Foaming Behavior of Poly(lactic Acid) with Different D-isomer Content Based on Supercritical CO2-induced Crystallization

Foaming of poly(lactic acid) using supercritical carbon dioxide as foaming agent: Influence of crystallinity and spherulite size on cell structure and expansion ratio

Enhancing the Antishrinkage and Mechanical Performances of the PBAT/PVA Foam for Environment-Friendly Packaging

Effects of Plasticizing on Mechanical and Viscous Characteristics of Poly(vinyl alcohol): A Comparative Study between Glycerol and Diethanolamine

Dual Role of PDMS on Improving Supercritical CO2 Foaming of Polypropylene: CO2-philic Additive and Crystallization Nucleating Agent

Foaming behavior of isotactic polypropylene in supercritical CO2 influenced by phase morphology via chain grafting

Effect of Foaming Temperature on Cell Structure of Foamed Polypropylene Using Supercritical CO2