Abstract:One prerequisite for the large-scale application of biodegradable polymers is the manipulation of macroscopic performances of commercially available biopolymers during processing according to different real service requirements. Herein, the microstructural evolution of poly(butylene adipate-co-butylene terephthalate) (PBAT) modified by chain extender during film blowing was investigated by in situ synchrotron radiation X-ray scattering to unveil the origin of different performances. The chain dynamics difference induced by the chain extender was first characterized by the rheological measurement and 1H Multiple Quantum (MQ) NMR. It shows that the terminal relaxation is significantly slowed down, while the locally segmental dynamics is not apparently changed. With the assistance of the custom-built film blowing apparatus, the microstructure right above the die exit (D = 13-165 mm) was in situ, simultaneously captured by small- and wide-angle scattering (SAXS/WAXS), where four distinct regimes can be defined. Only the PBAT melt signals are found in regime I, whereas the formation of the mesomorphic domains as shown by the SAXS streaks appearing in regime II. The crystal shows up in regime III, where the WAXS signal appears. A dramatic increment of the crystallinity is found in regime III, which contributes to the continuous increasing bubble modulus with the formation of the crystal-based network. Such a crystal-based network is filled with crystals in regime IV, where the diameter of the PBAT bubble remains constant. The addition of the chain extender is found to significantly influence the structural evolution within different regimes. These dynamics and structure information could supply general guidance for bubble stability improvement and modification of macroscopic performances of biodegradable polymer products.

Foaming Behaviors of Poly (butylene Adipate-Co-terephthalate) with Methyl Methacrylate-Co-glycidyl Methacrylate As Chain Extender

Synthesis and Thermomechanical and Rheological Properties of Biodegradable Long-Chain Branched Poly(Butylene Succinate-Co-Butylene Terephthalate) Copolyesters

Polybutylene adipate terephthalate/polylactic acid interface enhanced compatibilization and its bead-foaming characteristics

High-Strength Bio-Degradable Polymer Foams with Stable High Volume-Expansion Ratio Using Chain Extension and Green Supercritical Mixed-Gas Foaming

An Ultra-High Volume Expansion Ratio and No-Shrinkage Poly(Butylene Adipate-co-Terephthalate) Foam: Compression and Resilience Properties

Study on the Foaming Behaviors of PBS and its Modification with PA6IcoT Assisted by scCO2

Dynamic Cross-linked Poly(butylene adipate- co -terephthalate) for High-Performance Green Foam

Preparation of high melt strength polypropylene by the reactive extrusion process and its foaming application

The effect of free radical initiators on poly (butylene adipate-co-terephthalate) (PBAT) and its foaming performance

Super toughened blends of poly(lactic acid) and poly(butylene adipate- co -terephthalate) injection-molded foams via enhancing interfacial compatibility and cellular structure

Strategy for the Preparation of PBAT/Starch Blended Foam with High Resilience and Shrinkage Resistance

Biodegradable and Ultra-High Expansion Ratio PPC-P Foams Achieved by Microcellular Foaming Using CO2 as Blowing Agent

Bimodal Cellular Structure Evolution in PBAT Foams Incorporated by Carbon Nanotubes and Graphene Nanosheets

Manipulation of Chain Entanglement and Crystal Networks of Biodegradable Poly(butylene Adipate-Co-butylene Terephthalate) During Film Blowing Through the Addition of a Chain Extender: an in Situ Synchrotron Radiation X-ray Scattering Study.

Green preparation of poly (butylene succinate-co-butylene terephthalate) foam with tunable degradability and mechanical properties by supercritical CO2

Effect of chain extender on the morphological, rheological and mechanical properties of biodegradable blends from PBAT and P34HB

Reinforcing a Thermoplastic Starch/Poly(butylene adipate-co-terephthalate) Composite Foam with Polyethylene Glycol under Supercritical Carbon Dioxide

Interfacial interaction enhancement between biodegradable poly (butylene adipate-co-terephthalate) and microcrystalline cellulose based on covalent bond for improving puncture, tearing, and enzymatic degradation properties

Synthesis of Poly(butylene adipate terephthalate)- co -poly(glycolic acid) with Enhanced Degradability in Water

A Novel Method for Preparing Microcellular PBAT/GNPs Foam with High Volume Expansion Ratio: Effect of Vacuum Foaming

Preparation of carbodiimide-mediated octadecylamine modified carboxyethyl cellulose microfibrils and their reinforcement of poly(butylene adipate-co-terephthalate)