Abstract:Polyesters based on 2,5-furandicarboxylic acid (2,5-FDCA) have attracted attention from both academia and industry as a new class of biobased polymers for the growing era of plastics. 2,5-FDCA-based polyesters are 100% renewable, and they are an alternative to petroleum-based or terephthalic acid (TPA)-based polyesters. Moreover, scientists and plastics experts have recognized bioplastics as an eco-friendly solution to developing cost-effective renewable plastics. The growth of the bioplastics market depends on a sustainable economy, population growth, and rapid changes in different polymers. Although a variety of auxiliaries have been practically used in recent years, the production of bioplastics from 2,5-FDCA monomers by oxidation of 5-hydroxymethylfurfural (HMF) is a relatively innovative field of research. This review focuses on the properties and applications of 2,5-FDCA-based polyesters in the packaging and coating industries for producing biobased postconsumer products. The manufacturability, excellent (thermal, mechanical, and barrier) features, and applications in various fields of available 2,5-FDCA-based homo- and copolyesters are discussed. Biobased 2,5-FDCA pure homo- and copolyesters have recently progressed with exceptional properties for their counterparts petroleum-based polyesters. In particular, the mechanical performance of 2,5-FDCA-based pure homopolyesters such as poly(ethylene 2,5-furandicarboxylate) (PEF) and poly(propylene 2,5-furandicarboxylate) (PPF) has the highest tensile strength (σ b) values of 84.07 ± 4.43 and 90 ± 6 MPa, respectively, compared with other homopolyesters. On the other hand, 2,5-FDCA-based neat copolyesters like poly(ethylene 2,5-thiophenedicarboxylate) (PETF) and poly(ethylene-co-1,4-cyclohexanedimethylene 2,5-furandicarboxylate) (PECF) had maximum tensile strength (σ b) values of 97–98 and 59–75 MPa, respectively, compared to other copolyesters. In addition, we also compared and observed the highest Young’s modulus (E) values of pure PEF (5248 ± 328 MPa) and pure PPF (2460 ± 280 MPa) homopolyesters and of neat PETF (3100–3300 MPa) and neat PECF (1740–2300 MPa) copolyesters. Furthermore, the elongation at break (ε b) values of pure poly(decylene furandicarboxylate) (PDF) (986 ± 82%) and pure poly(butylene 2,5-furandicarboxylate) (PBF) (368 ± 43%) homopolyesters and neat poly(pentylene furandicarboxylate) (PPeF) (1050 ± 200%) and neat poly(1,4-butanediol 2,5-thiophenedicarboxylate) (PBTF) (900 ± 84%) copolyesters had the highest values compared to other pure homo- and copolyesters. Finally, the results of the barrier improvement factor (BIFp) study showed that neat PPeF copolyesters had the highest values of O2 (227 BIFp) and CO2 (979 BIFp) compared to other pure homo- and copolyesters.

Biobased Poly(ethylene-co-hexamethylene 2,5-Furandicarboxylate) (PEHF) Copolyesters with Superior Tensile Properties

Modification of Poly(ethylene 2,5-Furandicarboxylate) with Biobased 1,5-Pentanediol: Significantly Toughened Copolyesters Retaining High Tensile Strength and O2 Barrier Property

Modification of Poly(ethylene 2,5-Furandicarboxylate) with Aliphatic Polycarbonate Diols: 1. Randomnized Copolymers with Significantly Improved Ductility and High CO2 Barrier Performance

Poly(ethylene 2,5-Furandicarboxylate-mb-poly(tetramethylene Glycol)) Multiblock Copolymers: from High Tough Thermoplastics to Elastomers

Modification of Poly(ethylene furandicarboxylate) with Aliphatic Polycarbonate diols: 1. Randomnized Copolymers with Significantly Improved Ductility and High CO2 Barrier Performance

DBU-catalyzed biobased poly(ethylene 2,5-furandicarboxylate)polyester with rapid melt crystallization : synthesis, crystallization kinetics and melting behavior

Biobased poly(butylene 2,5-furandicarboxylate) and poly(butylene adipate-co-butylene 2,5-furandicarboxylate)s: From synthesis using highly purified 2,5-furandicarboxylic acid to thermo-mechanical properties

In-situ Synthesis, Thermal and Mechanical Properties of Biobased Poly(ethylene 2,5-Furandicarboxylate)/montmorillonite (PEF/MMT) Nanocomposites

Biobased 1,5-Pentanediol Derived Aliphatic-Aromatic Copolyesters: Synthesis and Thermo-Mechanical Properties of Poly(pentylene Succinate-Co-terephthalate)s and Poly(pentylene Adipate-Co-terephthalate)s

High Molecular Weight Polyesters Derived from Biobased 1,5-Pentanediol and a Variety of Aliphatic Diacids: Synthesis, Characterization, and Thermo-Mechanical Properties

Thermal and Mechanical Properties of Ultrahigh-Molecular-Weight Ethylene/1-Hexene Copolymers Prepared by Living Polymerization with Fluorinated Bis(Phenoxy-Imine) Titanium(Iv) Catalyst

Synthesis and properties of poly(ethylene‐co‐diethylene glycol 2,5‐furandicarboxylate) copolymers

Synthesis and characterization of biobased copolyesters based on pentanediol: (1) Poly(pentylene dodecanoate‐co‐furandicarboxylate)

New Bio-Based Copolyesters Derived from Novel Cyclic Diol 2,5-Tetrahydrofurandimethanol, 2,5-Furardicarboxylic Acid and 1,3-Propanediol: Synthesis, Thermal Behavior and Rheological Properties

Aliphatic polycarbonate modified poly(ethylene furandicarboxylate) materials with improved ductility, toughness and high CO2 barrier performance

Fully bio-based polyesters poly(ethylene-co-1,5-pentylene 2,5-thiophenedicarboxylate)s (PEPTs) with high toughness: Synthesis, characterization and thermo-mechanical properties

Recent Progress on Sustainable 2,5-Furandicarboxylate-Based Polyesters: Properties and Applications

Poly(ether‐ester)s synthesized from furandicarboxylic acid and ethylene glycol using an acidic binary catalyst

Synthesis of high-T fluorinated polyesters based on 2,5-furandicarboxylic acid

Synthesis and characterization of fluorine-containing polyester based on phthalic anhydride and tetrafluoropropyl glycidyl ether

Synthesis, Thermal Behavior, and Mechanical Properties of Fully Biobased Poly(Hexamethylene 2,5-Furandicarboxylate-Co-Sebacate) Copolyesters