Abstract:Homogenously doped and mixed yttria stabilized zirconia, YSZ (with 3 and 10mol% Y2O3 known as 3YSZ and 10YSZ) and NiO/10YSZ co-precipitates (nominally corresponding to 7, 12, 24, 30, 35 and 45vol.% Ni metal), were synthesized using a continuous hydrothermal flow synthesis (CHFS) system which uses a stream of superheated water at 450°C and 24.1MPa as a reaction medium to cause rapid precipitation of metal oxide nanoparticle co-precipitates from a mixed metal salt solution. All products were obtained directly from the outlet of the CHFS reactor as a slurry, which was then cleaned and freeze-dried prior to further processing. The highly crystalline nano-powdered products were characterized using a range of analytical methods, including: powder X-ray diffraction (XRD), energy dispersive spectroscopy (EDS), transmission electron microscopy (TEM), Raman spectroscopy and BET surface area measurements. Spherical primary particles of 10YSZ and 3YSZ were observed under the TEM and found to be 5.0±0.8nm (range 3.2–6.3nm) and 6.2±1.4nm (range 3.3–8.4nm) in size, with measured BET surface areas of 160.6 and 241.7m2g−1, respectively. Sintering of the nano-powder co-precipitates was performed via spark plasma sintering (SPS) at 1100°C for 1min, leading to densities of ca. 98% for 10YSZ and ca. 96% for Ni/10YSZ cermets (all NiO was converted into Ni due to the reducing atmosphere of the SPS). The 24% Ni/10YSZ cermet was subjected to focused ion beam tomography, which allowed the 3D arrangement of the conducting Ni metallic network of the dense cermet to be elucidated, and showed that a complete 3D network of Ni existed throughout the dense cermet disk. Electrical conductivity tests showed that the samples exhibited higher than expected electrical conductivity (for such low metal content), e.g., the 24vol.% Ni-containing sample achieved an electrical conductivity of ∼200Scm−1 at the fuel cell operating temperature, which corresponds to an effective conductivity of ∼117Scm−1 if a porosity of 30% were to be introduced.

Electrical Conductivity of Inhomogeneous Cu2O–10CuAlO2–xCu Cermets

Mechanical and Physical Properties of Cu2O−xCu Cermet

Cu2O/Cu Cermet As a Candidate Inert Anode for Al Production

P-type Transparent Conducting Copper Aluminum Oxide Films with Different Cu/Al Ratio

Electric conductivity and percolation threshold research of Cu-Cu2O cermet

Exploring Cu2O/Cu Cermet As a Partially Inert Anode to Produce Aluminum in a Sustainable Way

Microstructure and Mechanical Property of Cu2O–Cu Cermet Prepared by In-Situ Reduction-Hot Pressing Method

Effect of Metallic Phase on Relative Density of NiFe_2O_4-10NiO Based Cermet for Aluminum Electrolysis

Effect of metallic content on sintering behavior of NiFe2O4-based cermet inert anode for aluminum electrolysis

Influence of the Metal Particle Size and Sintering Process on the Electrical Resistivity of M-Zro2/30%mo Cermet

Densification of Ni-NiFe2O4 cermets for aluminum electrolysis

Sintering Densification of Cu/Al2O3p Nano-Composite Powders by Electroless Copper Plating

Ultrafast pressureless sintering of high conductivity Ni-based cermets inert anode for Carbon‐free electrolytic aluminum

Materials Fabrication and Corrosion Behavior of NiFe2O4 Cermet Inert Anodes

On the corrosion behaviour of NiFe2O4-NiO based cermets as inert anodes in aluminum electrolysis

Highly conductive low nickel content nano-composite dense cermets from nano-powders made via a continuous hydrothermal synthesis route

Microstructure and Properties of Ti(C,N)-Based Cermets with AlxCoCrFeNiTi Binder

Fabrication of W–Cu/CeO2 Composites with Excellent Electric Conductivity and High Strength Prepared from Copper-Coated Tungsten and Ceria Powders

Comparative Study on Electrical Conductivity of CeO2-Doped AlN Ceramics Sintered by Hot-Pressing and Spark Plasma Sintering

Microstructure and property of electroformed nano-Al2O3/Cu composite

Microstructure and Properties of Porous Ni50Cr50- Al2O3 Cermet Support for Solid Oxide Fuel Cells