Influence of AlN addition on the microstructure, mechanical properties and oxidation characteristics of NbC-Ni cermets

Jiyong Yi,Sixing Xie,Li Chen,Dike Yan

DOI: https://doi.org/10.1016/j.ijrmhm.2023.106426

IF: 4.804

2023-10-12

International Journal of Refractory Metals and Hard Materials

Abstract:Herein, NbC–Ni cermets with various AlN contents (0–9.0 wt%) are prepared using powder metallurgy, and their microstructure, mechanical properties, and oxidation characteristics are investigated. The addition of AlN dissolves the binder and forms Ni 3 Al, which can inhibit the dissolution–reprecipitation process and refine the average grain size of NbC, thereby resulting in enhanced mechanical properties of the cermets. Cermets with 1.0 wt% AlN exhibit the highest hardness (HV 10 1,470 kg/mm 2 ) and TRS (1365 MPa). With an increase in AlN content, excess Al exists as a metallic phase in the cermets. This destroys the continuity of the cermet structure and decreases its hardness and transverse rupture strength. For oxidation test at 700 °C, NbC in the cermets is oxidized primarily to Nb 2 O 5 , and the Ni binder is transformed into binary oxides, such as (NiNb 2 O 6 ) 0.6667 . The oxidation weight gain of the NbC cermets decreases after the addition of AlN, which can be attributed to the formation of Ni 3 Al, thus slowing the oxidation of the binder. Further addition of AlN up to 3.0 wt% deteriorated the oxidation resistance because cracks were generated at the boundary of the Nb 2 O 5 /Al 2 O 3 interface, which accelerated the oxidation process.

materials science, multidisciplinary,metallurgy & metallurgical engineering