Abstract:This paper reports the development of TiCN - Co - Cr3C2 - Si3N4 cermets modified with the addition of B4C. Cermets of three different compositions with varying B4C in TiCN - Co - Cr3C2 - Si3N4 were fabricated. The TiCN, Co, Cr3C2, Si3N4 and B4C powders in the combinations 80%TiCN-5%Co-5%Cr3C2–5%Si3N4–5%B4C; 75%TiCN-5%Co-5%Cr3C2–5%Si3N4–10%B4C; 70%TiCN-5%Co-5%Cr3C2–5%Si3N4–15%B4C were ground in a ball milling unit for six hours at a speed of 300 rpm at a ball-to-powder ratio of 10:1. The powders were then sintered in a vacuum hot press at a temperature of 1600 °C and a pressure of 50 MPa with soaking time of 90 min. For comparison purpose, 90%TiCN-5%Co-5%Cr3C2 cermet was prepared. The microstructure of the sintered cermets revealed the core-rim structure. The Vickers hardness test was done with a load of 10 Kg and for duration of 10 s. Fracture toughness was measured using the crack length data obtained from the hardness test using scanning electron microscopy. The cermet with a composition 75% TiCN-5%Co-5% Cr3C2–5% Si3N4–10% B4C produced higher hardness of 26.53 ± 0.56 GPa and fracture toughness of 10.29 ± 0.18 MPa m and 70% TiCN-5%Co-5% Cr3C2–5% Si3N4–15% B4C showed high fracture toughness value of 11.23 ± 0.09 MPa m with hardness value of 21.05 ± 0.10 GPa. The cermet composition 75% TiCN-5%Co-5% Cr3C2–5% Si3N4–10% B4C retained the hardness of 16.85 GPa even after annealing at 600 °C. The sintered cermets tend to form TiO2 which determines the hardness of the annealed cermets at a range of 600 °C – 1000 °C. The presence of these oxides tends to decrease the hardness. The wear test was performed taking the cermet as the pin material. The abrasive and adhesive wear mechanisms were dominant in the cermets. The harder precipitates formed tend to increase wear resistance by reducing the wear rate. The harder precipitates (TiN and TiB2) formed mainly due to the addition of Si3N4 and B4C, this addition promotes adhesive wear by a tribolayer formation.

Strengthening and toughening of Ti(C,N)-based cermets: (Ti,W)C additive design and the mechanism

Influence of TaC content on microstructure and mechanical performance of Ti(C,N)-based cermets fabricated by mechanical activation and subsequent in situ carbothermal reduction

Achieving hardness‐strength‐toughness synergy in (Ti, W, Mo, Cr)(C, N)‐based cermets

Correlation between microstructure and mechanical properties of Ti(C,N)-xWC-Ni cermets prepared by mechanical activation and subsequent in situ carbothermal reduction

Evolution of microstructure and interfacial characteristics of complete solid-solution Ti(C,N)-based cermets fabricated by mechanical activation and subsequent in situ carbothermal reduction

Fabrication, microstructure evolution, and mechanical properties of Ti(C,N)-HfN-WC-Ni-Mo cermets

Microstructure and properties of Ti(C, N)-based cermet with multi-core-rim microstructure: effect of (Ti, W, Ta) (C, N) pre-solid solution composition

Microstructure and Properties of Ti(C,N)-Based Cermets with AlxCoCrFeNiTi Binder

Insights into Hardening and Strengthening in Ultrafine Ti(C, N)-Based Cermets

Microstructure and Mechanical Properties of TiC Reinforced NbC-Ni4VC4Mo2C Cermets

Formation of solid solution structures in (Ti,W,Ta,Mo)(C,N) cermet via spark plasma sintering

Improvement of microstructure, mechanical properties and cutting performance of Ti(C,N)-based cermets by ultrafine La2O3 additions

Effects of the addition of multi-walled carbon nanotubes on the microstructure and properties of Ti(C,N)-based cermets prepared by spark plasma sintering

Strengthening and toughening mechanism of (W,Ti,Ta)C based cermet with the addition of c-BN@Al2O3

Tuning microstructure for superb mechanical properties in a Ti(C,N)-(WMoTaNbTi)C-Ni/Co cermets via change sintering temperature

Ultra-High Hardness TiC-W-Ni Cermets Prepared by Spark Plasma Sintering of Ultra-Fine TiC Powder

Effects of CrMnFeCoNi additions on microstructure, mechanical properties and wear resistance of Ti(C,N)-based cermets

Effect of Y2O3 Addition on the Microstructure and Mechanical Properties of TiCN-based Cermets

Manipulating interface bonding and microstructure via tuning interfacial reaction for enhancing mechanical property of in-situ TiC/Al cermets

Preparation and properties of Ti(C,N)-based cermets with graphene nanosheet addition by spark plasma sintering

On the effects of B4C addition on the microstructure, mechanical properties, wear and thermal stability of TiCN- co -Cr3C2-Si3N4 cermets developed by vacuum hot pressing