Abstract:This paper reports the development of TiCN - Co - Cr3C2 - Si3N4 cermets modified with the addition of B4C. Cermets of three different compositions with varying B4C in TiCN - Co - Cr3C2 - Si3N4 were fabricated. The TiCN, Co, Cr3C2, Si3N4 and B4C powders in the combinations 80%TiCN-5%Co-5%Cr3C2–5%Si3N4–5%B4C; 75%TiCN-5%Co-5%Cr3C2–5%Si3N4–10%B4C; 70%TiCN-5%Co-5%Cr3C2–5%Si3N4–15%B4C were ground in a ball milling unit for six hours at a speed of 300 rpm at a ball-to-powder ratio of 10:1. The powders were then sintered in a vacuum hot press at a temperature of 1600 °C and a pressure of 50 MPa with soaking time of 90 min. For comparison purpose, 90%TiCN-5%Co-5%Cr3C2 cermet was prepared. The microstructure of the sintered cermets revealed the core-rim structure. The Vickers hardness test was done with a load of 10 Kg and for duration of 10 s. Fracture toughness was measured using the crack length data obtained from the hardness test using scanning electron microscopy. The cermet with a composition 75% TiCN-5%Co-5% Cr3C2–5% Si3N4–10% B4C produced higher hardness of 26.53 ± 0.56 GPa and fracture toughness of 10.29 ± 0.18 MPa m and 70% TiCN-5%Co-5% Cr3C2–5% Si3N4–15% B4C showed high fracture toughness value of 11.23 ± 0.09 MPa m with hardness value of 21.05 ± 0.10 GPa. The cermet composition 75% TiCN-5%Co-5% Cr3C2–5% Si3N4–10% B4C retained the hardness of 16.85 GPa even after annealing at 600 °C. The sintered cermets tend to form TiO2 which determines the hardness of the annealed cermets at a range of 600 °C – 1000 °C. The presence of these oxides tends to decrease the hardness. The wear test was performed taking the cermet as the pin material. The abrasive and adhesive wear mechanisms were dominant in the cermets. The harder precipitates formed tend to increase wear resistance by reducing the wear rate. The harder precipitates (TiN and TiB2) formed mainly due to the addition of Si3N4 and B4C, this addition promotes adhesive wear by a tribolayer formation.

Strengthening and toughening mechanism of (W,Ti,Ta)C based cermet with the addition of c-BN@Al2O3

Strengthening and toughening of Ti(C,N)-based cermets: (Ti,W)C additive design and the mechanism

Formation of solid solution structures in (Ti,W,Ta,Mo)(C,N) cermet via spark plasma sintering

Achieving hardness‐strength‐toughness synergy in (Ti, W, Mo, Cr)(C, N)‐based cermets

Synthesis and characterization of Mo@Ni core-shell composite powder-reinforced (W,Ti)C-based cermet

Microstructure and strengthening mechanism of Mo@Ni reinforcement (W,Ti)C cermet via spark plasma sintering

Synthesis and characterization of extremely hard and strong (W,Ti,Ta)C cermet by spark plasma sintering

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

Production of high-property Cr3C2-based cermet with Cr3C2–10WC composite powder as starting material

Ultra-toughened Al2O3–TiC–Co ceramic

High-pressure Synthesis of Al2O3-cBN Composites: Effect of Thermodynamic Condition and Cbn Volume Fraction on Their Microstructure and Properties

Microstructure and Properties of Ti(C,N)-Based Cermets with AlxCoCrFeNiTi Binder

The improvement mechanism of mechanical properties of B4C ceramics by constructing core‐shell powders

Microstructure and Mechanical Properties of TiC Reinforced NbC-Ni4VC4Mo2C Cermets

Synthesis of TiB 2 /Ti(C,N) cermet by RSPS: formation mechanism, shrinkage behavior, and mechanical properties

A strong, ductility maintained, and high-temperature resistant Ti-based composite with TiC@(TiCr 2 +α-Ti) reinforced particles

On the effects of B4C addition on the microstructure, mechanical properties, wear and thermal stability of TiCN- co -Cr3C2-Si3N4 cermets developed by vacuum hot pressing

A novel core-shell TiCx particle by modifying TiCx with B element and the preparation of the (TiCx + AlN)/Al composite

Microstructure and properties of Ti(C, N)-based cermet with multi-core-rim microstructure: effect of (Ti, W, Ta) (C, N) pre-solid solution composition

Preparation and properties of Ti(C,N)-based cermets with graphene nanosheet addition by spark plasma sintering

Preparation and toughness mechanism of in-situ Ti3AlC2 enhanced and toughened TiAl3 matrix composites