Abstract:The quality of injection molded polymer products can be compromised due to the occurrence of residual stresses inherent to the molding process. In order to determine the parameters that influence the dimensional changes and residual stresses of injection molded polypropylene; computer simulations, chemical, thermal and mechanical characterizations were performed. Statistically, we evaluated two conditions of part geometry (with and without rib), three holding pressures (25, 60 and 96 MPa) and three post-molding conditions (without restriction, with restriction followed by water, and with restriction followed by annealing). The specimens molded with ribs and lower holding pressures showed greater warpage, which agreed with the computer simulations. The smooth specimens submitted to annealing followed by air cooling showed lower warpage in relation to the other two post-molding conditions. The thermal analysis presented a lower degree of crystallinity in the samples without post-molding restrictions. The samples submitted to the annealing heat treatment showed an increase in impact strength, and there was no significant variation in the modulus of elasticity for the post-molding conditions evaluated. The ribbed specimens exhibited higher residual stresses than the smooth specimens. Samples with greater warpage had lower residual stresses. All samples showed a tensile-compression-tensile behavior along the hole depth. The results showed that the shrinkage values were not influenced by any of the parameters evaluated. However, on the warpage the factor that exerts the greatest influence is the geometry of the part, followed by the holding pressure; and the post-molding condition presented the least influence among the analyzed factors.

SHRINK AND DEFECT ANALYSIS OF HDPE THICK PART

The Influences of Cooling Rate on Shrink and Shrinkage Formation of HDPE Thick Parts

Effect on Residual Wall Thickness of Parts with Floating Core Injection of Water-Assisted Injection Molding

Simulation and Experimental Analysis on Non-circular Cross-section Parts Residual Wall Thickness of Water-assisted Injection Molding

Investigation of Mold Temperature Affecting on Shrinkage of Rapid Heat Cycle Molding Plastic Part

Development of High-Density-Polyethylene-Based Thick Multi-Reducer Injection Mold Incorporating Cooling Analysis Technology

Research on the Effects of Process Parameters on Shrinkage Variation of the Rapid Heat Cycle Molding Plastic Part

Influence of process parameters and post-molding condition on shrinkage and warpage of injection-molded plastic parts with complex geometry

Analysis of Defects of Micro Injection Molded PP Parts

3D Simulation of Residual Thermal Stress and Shrinkage in Plastic Injection Molding

The influence of mold design and process parameters on dimensional shrinkage of perfluoroalkoxy alkane injection molding parts

Warpage of Injection-Molded Thermoplastics Parts: Numerical Simulation and Experimental Validation

Numerical Study of Thickness Distribution of Stretch-Blow Bottles for Defects Prediction

Flow Simulation and Defects Analysis of Injection Molded Parts Based on CAE Technique

The Influence of Mold Pressing Parameters on Ptc of Hdpe/Cb Composites

Cavity Filling Analysis of Injection Molding Simulation:The Formation of Bubble and Weld Line

Dimensional Analysis Theory and Molecular Dynamics Simulation of Polypropylene Melt Flow during Injection Molding Process

Shrinkage and Warpage Mechanism of Overflow Water-Assisted Injection Molding Short Fiber-Reinforced Polymers

Integrated Simulation of Fluid Flow and Heat Transfer in Injection Molding for the Prediction of Shrinkage and Warpage

Experimental and numerical investigations on formation mechanisms of hollow structures in overflow water‐assisted injection‐molded parts of short‐glass‐fiber‐reinforced polypropylene

Application of Mold Flow Analysis Technology in Plastic Mold Analysis