Abstract:The quality of injection molded polymer products can be compromised due to the occurrence of residual stresses inherent to the molding process. In order to determine the parameters that influence the dimensional changes and residual stresses of injection molded polypropylene; computer simulations, chemical, thermal and mechanical characterizations were performed. Statistically, we evaluated two conditions of part geometry (with and without rib), three holding pressures (25, 60 and 96 MPa) and three post-molding conditions (without restriction, with restriction followed by water, and with restriction followed by annealing). The specimens molded with ribs and lower holding pressures showed greater warpage, which agreed with the computer simulations. The smooth specimens submitted to annealing followed by air cooling showed lower warpage in relation to the other two post-molding conditions. The thermal analysis presented a lower degree of crystallinity in the samples without post-molding restrictions. The samples submitted to the annealing heat treatment showed an increase in impact strength, and there was no significant variation in the modulus of elasticity for the post-molding conditions evaluated. The ribbed specimens exhibited higher residual stresses than the smooth specimens. Samples with greater warpage had lower residual stresses. All samples showed a tensile-compression-tensile behavior along the hole depth. The results showed that the shrinkage values were not influenced by any of the parameters evaluated. However, on the warpage the factor that exerts the greatest influence is the geometry of the part, followed by the holding pressure; and the post-molding condition presented the least influence among the analyzed factors.

3D Simulation of Residual Thermal Stress and Shrinkage in Plastic Injection Molding

Residual stresses, shrinkage, and warpage of complex injection molded products: Numerical simulation and experimental validation

Simulation and Experimental Analysis on Non-circular Cross-section Parts Residual Wall Thickness of Water-assisted Injection Molding

Effect on Residual Wall Thickness of Parts with Floating Core Injection of Water-Assisted Injection Molding

Integrated Simulation of Fluid Flow and Heat Transfer in Injection Molding for the Prediction of Shrinkage and Warpage

3D Simulation of Filling Stage of Plastic Injection Molding Based on Improved Finite Volume Method

Local thermal warpage deformation of polypropylene injection molded flat part and neural network prediction model

Influence of process parameters and post-molding condition on shrinkage and warpage of injection-molded plastic parts with complex geometry

INTEGRATED SIMULATION OF MELT FLOW, FIBER FRACTURE AND FIBER ORIENTATION FOR FIBER REINFORCED PLASTICS IN INJECTION MOLDING

COUPLING SIMULATION MODEL OF MELT FLOW AND FIBER ORIENTATION FOR FIBER REINFORCED PLASTICS IN INJECTION MOLDING

A dual‐scale three‐dimensional thermo‐viscoelastic model for the hot stamping simulation of thermoplastic composites

Numerical Optimization of Shrinkage and Warpage on the Injection Molding Process Parameters of Electrical Connector

Dispersed Phase Deformation Modeling of Immiscible Polymer Blends in Injection Molding

Cavity Filling Analysis of Injection Molding Simulation:The Formation of Bubble and Weld Line

Simulation of composite polymerization shrinkage using 3D finite element model

Computer Simulation Analysis of Ceramic Powder Injection Molding Process and Molding Defects Formation

Three-dimensional Finite Element Analysis of Process-Induced Residual Stress in Resin Transfer Molding Process

A three-dimensional viscoelastic analysis of thermoplastic resin matrix composite laminates during hot stamping

Non-isothermal simulation on injection/mold temperatures in liquid composite molding process

3D Flow Simulation for Viscous Nonisothermal Incompressible Fluid in Injection Molding

Influence of Injection Molding Conditions on Residual Stress in Sandwich Parts