Abstract:The stress corrosion behavior of 7xxx series aluminium alloys in different concentrations NaCl solution was studied, and numerical simulation was conducted in COMSOL Multiphysics based on experimental results. Different stresses were applied on the experiment pieces, the pitting crater deepened with the change of stress level. The corrosion rate increased with the raising stress. There is no positive correlation between stress corrosion degree and chloride ion concentration. The most severe corrosion occurs in 5.0 wt% NaCl solution instead of 6.0 wt% NaCl solution due to the increase of water film conductivity and decrease of solubility of oxygen under high Cl- environment. The finite element model was used to analyze the stress distribution on aluminium alloy surface, to describe the dynamic equation of anodic dissolution of metal due to elastic and plastic deformation. Corrosion occurs mainly in stress concentrated areas. When the stress loading exceeds a certain threshold, plastic strain occurs on the surface of both the specimen and the structural part, the corrosion current density increases instantaneously, and the corrosion behavior in the stress concentration area gradually intensifies. The survey can provide practical theoretical guidance for predicting stress corrosion and extending the service life of equipment in (harsh) marine environments.

Study on Stress Corrosion Property of 304 Austenitic Stainless Steel in the Environment of Acid Chloride Solution

Anomalous Evolution of Corrosion Behaviour of Warm-Rolled Type 304 Austenitic Stainless Steel

Study on stress corrosion behavior of 316L austenitic stainless steel in hot NaOH solution

Study on Corrosion Fatigue Behavior of 304L Austenite Stainless Steel in 325 °C High-Temperature Water Environment

Towards Understanding Stress Corrosion Cracking of Austenitic Stainless Steels Exposed to Realistic Sea Salt Brines

Experimental Investigation of Stress Corrosion Characteristics for 16mnr Steel in Nitrate Solution

CORROSION BEHAVIOR OF STAINLESS STEEL 304 AS WATER SUPPLY MATERIAL IN WATER CONTAINING CHLORIDE

Discussion on Factors of Unstable 304 Stainless Steel Stress Corrosion Cracking

Abnormal Evolution of Pitting Behavior of Warmly Pre-Strained Austenitic Stainless Steels

Electrochemical Study on the Impact of Nacl Impurity on Corrosion of Stainless Steel 316l in Molten Nitrate Salts for Thermal Energy Storage

On the corrosion cracking of austenitic stainless steel in molten solar salt: Experiments and modeling

The Study of Corrosion Behavior and Hardness of AISI Stainless Steel 304 in Concentration of Chloride Acid Solution and Temperature Variations

Environmentally assisted stress corrosion cracking behaviour of low alloy steel in SO 2 -containing NaCl solution

Study on High-Temperature Naphthenic Acid Corrosion of Type 304 and Type 316L Stainless Steel and Their Welded Joints

Effects of chloride on electrochemical and stress corrosion cracking behavior of 9Cr ferritic–martensitic steel

Corrosion of high-strength steel in 3.5% NaCl solution under hydrostatic pressure: Initial corrosion with tensile stress coupling

INFLUENCE OF Cl- ON CRITICAL PITTING TEMPERATURE FOR 304 AND 316 STAINLESS STEELS

Relationship Between the Martensite Phase Transition and Pitting Susceptibility of AISI-321 Stainless Steel in Acidic Solutions of NaCl

The influence Cl- on stress corrosion of 7 xxx series aluminium alloys studied by experimental and simulation technology

Corrosion of high-strength steel in 3.5% NaCl solution under hydrostatic pressure: understanding electrochemical corrosion with tensile stress coupling

Inhibition Effects of L−and L2on Stress Corrosion Cracking of Stainless Steel in Acidic Chloride Solutions