Abstract:Electrochemical noise data generated during the stress corrosion cracking (SCC) experiments under free corrosion potential performed on a high-strength carbon steel exposed to acidified sodium chloride solution and poisoned with sodium sulfide have been statistically analyzed. The electrochemical noise, observed as spontaneous potential fluctuations, was analyzed using the maximum entropy method and the discrete Fourier transform. In all the specimens tested, a low-frequency (LF) noise was obtained which characteristically indicated LF or flicker noise. Throughout the experiments, consistent noise behavior was observed, with the only significant perturbation being that associated with major transients that occurred when the specimens actually failed. In the statistical analysis of results, all the parameters used bear close correlations with the spectral density curves, noise amplitudes and the roll-off slopes. For this alloy, the results obtained from the electrochemical investigation and the scanning electron microscopy micrographs show the cracking behavior to be consistent with the hydrogen-induced cracking.

Environmentally assisted stress corrosion cracking behaviour of low alloy steel in SO 2 -containing NaCl solution

Environmentally assisted stress corrosion cracking behaviour of low alloy steel in SO2-containing NaCl solution

SCC Investigation of Low Alloy Ultra-High Strength Steel 30crmnsini2a in 3.5wt% NaCl Solution by Slow Strain Rate Technique

The stress corrosion cracking behavior of N80 carbon steel under a crevice in an acidic solution containing different concentrations of NaCl

Stress Corrosion Cracking of E690 Steel As a Welded Joint in a Simulated Marine Atmosphere Containing Sulphur Dioxide

Effect of Electrochemical Potential and Chloride Concentration on Stress Corrosion Cracking Behavior of 23co14ni12cr3mo Ultra-High Strength Steel in NaCl Solution

Comparative Evaluations on Stress Corrosion Cracking Mechanism of Low Alloy Ultra-High Strength Steels in Neutral 3.5 Wt% Nacl Solution

Strength Effect in Stress Corrosion Cracking of High-Strength Steel in Aqueous Solution

Experimental Study on Fatigue Crack Growth and Residual Strength of Steel 30crmnsini2a under Mixed Corrosive Environments

Effect of Anions on Stress Corrosion Cracking Behaviors of Ultra-High Strength Steel 23Co14ni12cr3mo

Evaluation of the Impact of Chloride Ion Concentration on Stress Corrosion Cracking in E690 Steel under Low Ph Conditions

Stress Corrosion Cracking Investigation of High Co-Ni Secondary Hardening Ultra-High Strength Steel in Neutral 3.5 Wt% NaCl Solution

Electrochemical Corrosion, Hydrogen Permeation and Stress Corrosion Cracking Behavior of E690 Steel in Thiosulfate-Containing Artificial Seawater

Threshold stress intensity of hydrogen-induced cracking and stress corrosion cracking of high strength steel

Influence of Different Heat-Affected Zone Microstructures on the Stress Corrosion Behavior and Mechanism of High-Strength Low-Alloy Steel in a Sulfurated Marine Atmosphere

Effect of High Cl<sup>-</sup> Environment on Stress Corrosion Cracking Behavior of M152 and 17-4PH High-strength Steels

Stress corrosion cracking behavior on carbon steel under the synergistic effect of chloride and bicarbonate ions in alternating wet-dry environment

Corrosion evolution and stress corrosion cracking behavior of a low carbon bainite steel in the marine environments: Effect of the marine zones

Investigation of Stress Corrosion Cracking Behaviors of an AZ91 Magnesium Alloy in 0.1 Kmol/m 3 Na2SO4 Solution Using Slow Strain Rate Test

Analysis of Electrochemical Noise Data of Stress Corrosion Cracking of High-Strength Carbon Steel in Acidified NaCl Solution

Study on the roles of bisulfite in the stress corrosion cracking of 7050-T7451 aluminum alloy in the thin electrolyte layer environment