Study on the roles of bisulfite in the stress corrosion cracking of 7050-T7451 aluminum alloy in the thin electrolyte layer environment

Mingtao Wang,Liwei Wang,Wendi Yang,Yuxi Liu,Herman Terryn,Zhongyu Cui

DOI: https://doi.org/10.1016/j.corsci.2023.111030

IF: 7.72

2023-05-01

Corrosion Science

Abstract:Effect of bisulfite (HSO3 -) on the stress corrosion cracking (SCC) behavior of 7050-T7451 aluminum alloy in the thin electrolyte layer environment in the presence of Cl- is investigated. Addition of HSO3 - inhibits the corrosion initiation but promotes the corrosion propagation and hydrogen uptake. With a quantitative calculation, the HSO3 - is demonstrated to significantly facilitate the synergistic effect between stress, corrosion, and hydrogen during the in-situ tensile test, resulting in the change of the SCC controlling step from corrosion-induced hydrogen to mechanical-electrochemical-hydrogen interactions. The buffer effect of HSO3 - plays a dominant role in the HSO3 --induced acceleration of the SCC degradation.

materials science, multidisciplinary,metallurgy & metallurgical engineering