Effects of composition and microstructure on oxidation and stress corrosion cracking susceptibility of stainless steel claddings in hydrogenated PWR primary water

Tongming Cui,Xinhe Xu,Jiarong Ma,Zhanpeng Lu,Yuanjie Tang,Kun Zhang,Shuangliang Yang,Zhiming Zhong,Sergio Lozano-Perez,Tetsuo Shoji
DOI: https://doi.org/10.1016/j.jnucmat.2021.153057
IF: 3.555
2021-09-01
Journal of Nuclear Materials
Abstract:<p>Oxidation resistance and stress corrosion cracking (SCC) susceptibility of A508Ⅲ-309L/308L stainless steel (SS) claddings were investigated in simulated pressurized water reactor (PWR) primary water following a microstructure characterization. Preferential oxidation of slip bands was observed in 309L SS. The oxidation resistance of 309L SS was found to be lower than that of 308L SS due to the higher Cr- and ferrite-content in 308L SS than in 309L SS after cladding. There was no indication of SCC for low alloy steel (LAS) after slow strain rate tensile (SSRT) tests. The presence of type-I and type-II boundaries, composition dilution and less δ-ferrite content synergistically contributed to increasing the SCC susceptibility of 309L SS cladding. The effect of chemical composition and microstructure on SCC performance of the SS claddings was discussed.</p>
materials science, multidisciplinary,nuclear science & technology
What problem does this paper attempt to address?