Abstract:NH4Cl corrosion failure often occurs in the overhead systems of hydrotreaters, and this failure is always accompanied by the appearance of H2S. A combination of electrochemical and surface spectroscopic (SEM/EDS, AFM, XRD) techniques was used to investigate the effect of different factors, including the surface roughness, temperature, dissolved oxygen, pH and H2S concentration, on the corrosion behavior of carbon steel in an NH4Cl environment with the presence of H2S. The effect of H2S concentrations (at the ppm level) on the corrosion behavior of carbon steel was systematically revealed. The experimental results clearly indicated that the corrosion rate reached a minimum value at 10 ppm H2S. The steel surface was covered by a uniform corrosion product film in a 10 ppm H2S environment, and the corrosion product film was tight and protective. The ammonia from NH4Cl helped maintaining the protectiveness of the corrosion films in this environment. Dissolved oxygen mainly accelerated the cathodic reaction. The cathodic limiting current density increased with increasing temperature, and the anodic branch polarization curves were similar at different temperatures. The anodic current density decreased as the pH decreased, and the cathodic current density increased as the pH decreased. The absolute surface roughness (R (a)) of carbon steel increased from 132.856 nm at 72 h to 153.973 nm at 144 h, and the rougher surface resulted in a higher corrosion rate. The critical innovation in this research was that multiple influential factors were revealed in the NH4Cl environment with the presence of H2S.

Effect of pH and applied stress on hydrogen sulfide stress corrosion behavior of HSLA steel based on electrochemical noise analysis

Effects of H2S/HS− on Stress Corrosion Cracking Behavior of X100 Pipeline Steel Under Simulated Sulfate-Reducing Bacteria Metabolite Conditions

Effect of CO2/H2S and Applied Stress on Corrosion Behavior of 15cr Tubing in Oil Field Environment

Investigation of the Effect of pH on Stress Corrosion Cracking of API 5L X65 Steel by Impedance Spectroscopy and Slow Strain Rate Tensile Test

Stress corrosion cracking behavior of X80 steel under the combined effects of sulfide and cathodic potential

Effect of Hydrogen Charging on the Stress Corrosion Cracking Behavior of X70 Steel in Simulated Deep Seawater Environment

Study on the roles of bisulfite in the stress corrosion cracking of 7050-T7451 aluminum alloy in the thin electrolyte layer environment

Hydrogen in Stress Corrosion Cracking of X-70 Pipeline Steels in Near-Neutral Ph Solutions

Identifying sulfide stress cracking stages on a HSLA pipeline steel in H2S environment by electrochemical noise

Effect of Hydrogen and Stress on Active Dissolution of 304 Stainless Steel in the Environment of Acid NaCl Solution

Accelerating Effect and Critical Ph Value of Occluded Cell Corrosion Within Pits, Crevices, or Stress Corrosion Cracks

INFLUENCE OF SATURATED H_2S ON CORROSION BEHAVIOR OF 316L STAINLESS STEEL

Microstructural Effects in the Development of Near-Neutral pH Stress Corrosion Cracks in Pipelines

Strength Effect in Stress Corrosion Cracking of High-Strength Steel in Aqueous Solution

Effects of Ph Value on the Stress Corrosion Cracking of Super 13cr Tubing Steel

Environmentally assisted stress corrosion cracking behaviour of low alloy steel in SO 2 -containing NaCl solution

Effect of mechanical stress on electrochemical corrosion of X65 carbon steel in CO2 saturated brine

A Study on the Corrosion Behavior of Carbon Steel Exposed to a H2S-Containing NH4Cl Medium

Effect of Hydrogen on Stress Corrosion Cracking of Magnesium Alloy in 0.1M Na2SO4 Solution

Effect of Service Environmental Parameters on Electrochemical Corrosion Behavior of L80 Casing Steel

Stress corrosion cracking behavior on carbon steel under the synergistic effect of chloride and bicarbonate ions in alternating wet-dry environment