GIANT DIELECTRIC CONSTANT MATERIAL CaCu3Ti4O12 PREPARED BY SOL-GEL METHOD

YANG Changhui,ZHOU Xiaoli,XU Gang,HANG Gaorong,WENG Wenjian,DU Piyi

DOI: https://doi.org/10.3321/j.issn:0454-5648.2006.06.024

2006-01-01

Abstract:CaCu3Ti4O12 ceramics with giant dielectric constants were successfully prepared by sintering at 950-1100 ℃ for 20h and using a powder prepared by the sol-gel method and calcined at 700-900 ℃ for 6-10 h. The phase structures of CaCu3Ti4O12 ceramics and precursor powders were measured by X-ray diffraction, and the morphology of CaCu3Ti4O12 ceramics was observed by scanning electron microscopy. The dielectric constant of CaCu3Ti4O12 was measured by an inductance-capacitance-resistance (ICR) meter at a frequency range from 10 Hz to 106 Hz. The results show that the dielectric constant of the CaCu3Ti4O12 ceramics is dependent on the grain size of the perovskite-like phase. The calcination temperatures of the precursor powders prepared by sol-gel method and the sintering temperature of CaCu3Ti4O12 ceramics are at least 100 ℃ lower than that by the traditional solid phase reaction process. A CaCu3Ti4O12 ceramic with a dielectric constant of 194753 was obtained by sintering at 1 100 ℃ and using the powder calcined at 800 ℃, which is much higher than that prepared by the traditional solid phase reaction process.