Abstract:CaCu3Ti4O12 (CCTO) ceramics have drawn much attention for their potential application in energy storage components and overvoltage protection devices. In order to improve the electrical properties and understand the colossal dielectric behavior, several CCTO ceramic samples were prepared and heat treated in different atmospheres. The results showed that the breakdown field and nonlinear coefficient were effectively intensified, and the dielectric loss was reduced after heat treatments in the oxidizing atmosphere including air and oxygen. However, CCTO phases will decompose into TiO2, CuO and CaTiO3 phases when heat treated in the neutral atmosphere such as nitrogen, losing its colossal dielectric behaviors and excellent electrical properties. It was found that the oxygen atmosphere played the most beneficial effect in improving the characteristics of CCTO ceramics in this research. The maximum stored energy density of CCTO can be promoted from 7.7 to 26.5 kJ/m(3), and the barrier height between grain boundaries were increased from 0.46 to 0.62 eV which may be closely related with its high breakdown filed. Three dielectric relaxations were observed in CCTO ceramics. After heat treatment in oxygen atmosphere, the activation energies of the two relaxation peaks (peak 1 and peak 2) in high frequencies kept nearly constant, at 0.11 and 0.51 eV respectively, while the activation energy of relaxation peak 3 at low frequency were enhanced from 0.75 to 0.85 eV, which may be related to the oxygen vacancy defects. Moreover, the contribution of dc conductivity to dielectric loss can be effectively restrained. An equivalent circuit model was proposed according to impedance analysis to expound the correlation between electrical properties and dielectric relaxations.

Effect of Oxygen Content on Giant Dielectric Constant and Dielectric Process in Cacu3ti4o12

Influence of sintering temperature on giant dielectric property of CaCu3Ti4O12

Study on the Origin of Giant Dielectric Constant of CaCu3Ti4O12 Ceramics

Investigation of the Size Effect on the Giant Dielectric Constant of CaCu 3 Ti 4 O 12 Ceramic

Electrical Resistance Transition of CaCu3Ti4O12 Ceramics Induced by Cyclic Voltammetry Conditioning

Influence of Sintering Atmosphere and Thermobaric Treatment (TBT) on Dielectric Behaviors of CaCu3Ti4O12 Ceramics

Effect of oxygen sintering atmosphere on the electrical behavior of CCTO ceramics

Dielectric and Impedance Performances of Giant Dielectric Constant Oxide Cacu3ti4o12

Investigation Of Size Effect On The Giant Dielectric Cacu3ti4o12 Ceramic

Dielectric properties and relaxation mechanism of CaCu3Ti4O12 ceramics

Effect of the Oxidizing Atmosphere on the Microstructure and Dielectric Properties of CaCu3Ti4O12 Ceramics

Structure and Dielectric Relaxations of CaCu3Ti4O12 Ceramics by Heat Treatments in Different Atmospheres

Grain-boundary and subgrain-boundary effects on the dielectric properties of CaCu<sub>3</sub>Ti<sub>4</sub>O<sub>12</sub> ceramics

Cacu3ti4o12 Films Prepared by Magnetron Sputtering

Dielectric Relaxation Behaviors of Pure and Pr6o11-Doped Cacu3ti4o12 Ceramics in High Temperature Range

Origin of the Temperature Stability of Dielectric Constant in CaCu3Ti4O12

Decrease of Dielectric Loss in Giant Dielectric Constant CaCu3 Ti4 O12 Ceramics by Adding CaTiO3

Ti deficiency effect on the dielectric response of CaCu3Ti4O12 ceramics

Influences of Cual2o4 Doping on the Dielectric Properties of Cacu3ti4o12 Ceramics

Calcination and sintering effects on the microstructure and dielectric properties of CaCu3Ti4O12 ceramics

Dielectric Properties of Cacu3ti4o12 Ceramics Prepared by A Simplified Coprecipitation Method