Dielectric Properties of Al2O3 Modified CaCu3Ti4O12 Ceramics
Y. Zhang,L. L. Xue,K. Zeng,X. W. Wang,L. Y. Sun,X. H. Meng,Y. C. Shi,Y. Y. Li,M. Z. Cao,Y. C. Hu,J. Shang,S. Y. Shang,S. Q. Yin
DOI: https://doi.org/10.1007/s10854-019-01810-2
2019-01-01
Abstract:In this work, CaCu3Ti4O12 modified by Al2O3 (w = 0, 0.05, 0.1, 1%) powders were prepared via a sol-gel process, and then the ceramics were prepared by conventional process using the obtained powders. The dependence of structure and properties of CaCu3Ti4O12 ceramics on the addition fractions of Al2O3 were studied. The results showed that the grain size and density of the samples greatly increase after modifying Al2O3. Moreover, all the samples exhibit giant dielectric properties (similar to 10(4)) and relatively low dielectric loss over a wide temperature and frequency range (20-200 degrees C, 10(2)-10(6) Hz). The giant dielectric properties of these samples could be explained by the internal barrier layer capacitance (IBLC) model, which consists of semiconducting grains and insulating grain boundaries. Specifically, the optimal Al2O3 modified CaCu3Ti4O12 (w = 0.05%) ceramic shows colossal permittivity (similar to 4.29 x 10(4)) and low dielectric loss (similar to 0.06) at room temperature and 1 kHz. The results indicated that the microstructures and dielectric properties of CaCu3Ti4O12 were significantly improved after modifying Al2O3.