Abstract:CaCu 3 Ti 4 O 12 (CCTO) nanomaterials were synthesized using the low-cost facile sol-gel technique. X-ray diffraction (XRD) patterns confirmed the cubic structure of the prepared sample. Scherrer's formula and the W-H (Williamson-Hall) plot was used to calculated the average crystallite size of the prepared sample and it was found to be 27 nm and 31.3 nm, respectively, while the strain created in the lattice is 5.008 × 10 −4 . Based on the absorbance plot, the band-gap ( E g ) of the sample was determined using Tauc's plot and it was found out to be 2.74 eV. The frequency dependence of dielectric permittivity ( ε ) and tangent loss ( tan δ ) of CCTO was analyzed at different temperature range from 300 K to 663 K over a frequency range from 10 Hz to 1 MHz. ε and tan δ decrease monotonically in entire frequency range and an anomalous frequency-dependent behavior was observed at different temperatures. High ε (in the range of 10 4 ) was found out at lower frequency range. Electrical conductivity was also analyzed in range of frequencies and temperature, it was found out that in higher region of frequency conductivity slightly increases. The room temperature values of ε , tanδ and conductivity was 7.5 × 10 3 , 1.5 and 0.4 × 10 −5 Ω −1 m −1 , respectively. The reduction in E g is achieved which was the major concern in this work. Furthermore, we have extensively studied the ε along with tan δ and ac conductivity for electronic application usage. According to these observations, CCTO is particularly prepared so that it could be suitable for microelectronic applications due to its high ε and low tan δ .

Preparation and characterization of CaCu 3 Ti 4 O 12 powders by non-hydrolytic sol–gel method

Preparation and characterization of CaCu3Ti4O12 powders by non-hydrolytic sol–gel method

Preparation and Characterization of Silica-Coated CaCu3Ti4O12

Oleic Acid Assisted Synthesis of CaCu3Ti4O12 Powders and Ceramics by Sol–gel Process

Microwave-Assisted Synthesis of High Dielectric Constant CaCu 3 Ti 4 O 12 from Sol–Gel Precursor

CaCu3Ti4O12 Ceramics from Basic Co-Precipitation (BCP) Method: Fabrication and Properties

Grain Size Effect on the Dielectric and Non-Ohmic Properties of CaCu3Ti4O12 Ceramics Prepared by the Sol-Gel Process

Dielectric Properties and IV Characteristic of CaCu_3Ti_4O_(12)-MgTiO_3 Composite Ceramic Synthesized by Sol-Gel Method

Structural and dielectric properties of CaCu3Ti4O12 synthesized by sol–gel method

Investigation of Phase Evolution of CaCu3Ti4O12 (CCTO) by in Situ Synchrotron High-Temperature Powder Diffraction

Preparation and Dielectric Properties of (ca0.61,nd0.26)tio3 Nanoparticles by a Sol–gel Method

Preparation of Tio2-Enriched Cacu3mn0.1ti3.9o12 Ceramics and Their Dielectric Properties

Structure, Properties, and Impedance Spectroscopy of CaCu3Ti4O12 Ceramics Prepared by Sol-Gel Process: Structure, Properties, and Impedance Spectroscopy of CaCu3Ti4O12

Preparation and properties of CaCu3Ti4O12 thick film by aerosol deposition method

Electrical Conduction and Dielectric Properties of the CaCu_3Ti_4O_(12) Ceramics Synthesized by SPS

Structure, Properties, And Impedance Spectroscopy Of Cacu3ti4o12 Ceramics Prepared By Sol-Gel Process

Effects of Carbon Coating on Microstructure and Dielectric Properties of Cacu3ti4o12

Microstructure and dielectric properties of Nd doped CaCu 3 Ti 4 O 12 synthesized by sol–gel method

Synthesis and Characterization of (pb,ca)tio3 Nanocrystalline Powders by Sol-gel Process

Calcining Temperature Dependence on Structure and Dielectric Properties of CaCu 3 Ti 4 O 12 Ceramics