Abstract:CaCu 3 Ti 4 O 12 (CCTO) nanomaterials were synthesized using the low-cost facile sol-gel technique. X-ray diffraction (XRD) patterns confirmed the cubic structure of the prepared sample. Scherrer's formula and the W-H (Williamson-Hall) plot was used to calculated the average crystallite size of the prepared sample and it was found to be 27 nm and 31.3 nm, respectively, while the strain created in the lattice is 5.008 × 10 −4 . Based on the absorbance plot, the band-gap ( E g ) of the sample was determined using Tauc's plot and it was found out to be 2.74 eV. The frequency dependence of dielectric permittivity ( ε ) and tangent loss ( tan δ ) of CCTO was analyzed at different temperature range from 300 K to 663 K over a frequency range from 10 Hz to 1 MHz. ε and tan δ decrease monotonically in entire frequency range and an anomalous frequency-dependent behavior was observed at different temperatures. High ε (in the range of 10 4 ) was found out at lower frequency range. Electrical conductivity was also analyzed in range of frequencies and temperature, it was found out that in higher region of frequency conductivity slightly increases. The room temperature values of ε , tanδ and conductivity was 7.5 × 10 3 , 1.5 and 0.4 × 10 −5 Ω −1 m −1 , respectively. The reduction in E g is achieved which was the major concern in this work. Furthermore, we have extensively studied the ε along with tan δ and ac conductivity for electronic application usage. According to these observations, CCTO is particularly prepared so that it could be suitable for microelectronic applications due to its high ε and low tan δ .

Structural and dielectric properties of CaCu3Ti4O12 synthesized by sol–gel method

Preparation and characterization of CaCu 3 Ti 4 O 12 powders by non-hydrolytic sol–gel method

Structure, Properties, And Impedance Spectroscopy Of Cacu3ti4o12 Ceramics Prepared By Sol-Gel Process

Electrical Conduction and Dielectric Properties of the CaCu_3Ti_4O_(12) Ceramics Synthesized by SPS

Structure, Properties, and Impedance Spectroscopy of CaCu3Ti4O12 Ceramics Prepared by Sol-Gel Process: Structure, Properties, and Impedance Spectroscopy of CaCu3Ti4O12

Impact of Co–Ni substitution on the structural and dielectric properties of calcium copper titanate

Preparation and characterization of CaCu3Ti4O12 powders by non-hydrolytic sol–gel method

Dielectric Properties and IV Characteristic of CaCu_3Ti_4O_(12)-MgTiO_3 Composite Ceramic Synthesized by Sol-Gel Method

Nanocomposite-Like Structure in an Epitaxial Cacu3ti4o12 Film on Laalo3(001)

Synthesis, characterization, and morphological control of CaCu3Ti4O12 through modify sol–gel method

Electrical Heterogeneity in CaCu3Ti4O12 Ceramics Fabricated by Sol–gel Method

Grain Size Effect on the Dielectric and Non-Ohmic Properties of CaCu3Ti4O12 Ceramics Prepared by the Sol-Gel Process

Study on structural, dielectric, and thermal behavior of CaCu3Ti4O12@CoFe2O4 composites

Microwave-Assisted Synthesis of High Dielectric Constant CaCu 3 Ti 4 O 12 from Sol–Gel Precursor

Giant Dielectric Permittivity and Non-Linear Electrical Behavior in CaCu3Ti4O12 Varistors from the Molten-Salt Synthesized Powder

Microstructure and Dc Conduction Properties of Cacu3 Ti4o12

Microstructure and dielectric properties of Nd doped CaCu 3 Ti 4 O 12 synthesized by sol–gel method

High Dielectric Permittivity and Low Dielectric Loss in Sol–gel Derived Zn Doped CaCu3Ti4O12 Thin Films

Optical Properties of High-Dielectric-constant CaCu3Ti4O12 Films

Dielectric Properties of Zr-Doped CCTO Based Ceramics Prepared via Sol-Gel Method

Preparation and Characterization of Silica-Coated CaCu3Ti4O12