Abstract:The Fe/Ti multilayers of nominal bilayer thickness of 4.0, 8.0 and 18.0 nm with alternating Fe and Ti sublayers thickness ratio of 1:1 were deposited by direct current magnetron sputtering on Si(100) substrates. The bilayer thickness of as-deposited Fe/Ti multilayers was measured as a modulation wavelength of 4.8, 8.5 and 19.0 nm, respectively, by small angle X-ray diffraction and cross-sectional transmission electron microscopy (XTEM). The three Fe/Ti multilayers were composed of pure metallic α-Fe and α-Ti according to wide angle X-ray diffraction and selected area diffraction. The Fe/Ti multilayers were in situ submitted to thermal vacuum annealing at the temperatures ranging from 523 K to 723 K for the annealing time of 3 h. With annealing at the lower temperature of 523 K, the intermetallic FeTi appeared in the Fe/Ti multilayers with small modulation wavelength of 4.8 nm. At 623 K, the intermetallic FeTi was formed with modulation wavelength of 8.5 nm. At the higher temperature of 723 K, the intermetallic FeTi was detected with modulation wavelength of 19.0 nm. The modulation wavelength of the Fe/Ti multilayers remained during the thermal annealing. The mixture of intermetallic FeTi and α-Fe phase was observed in the extended Fe sublayer of the Fe/Ti multilayers annealed at 723 K by XTEM, correspondingly the remaining Ti sublayer was obtained as a thinned sublayer. Coexistence of the intermetallic FeTi, α-Fe and α-Ti phases indicated that the dynamic factors have control of the intermixing between the Fe and Ti sublayers in the Fe/Ti multilayers during the thermal annealing.

Study on microstructure and interdiffusion behavior in Pb(Fe12Nb12)O3/Pt/Ti/SiO2/Si(100) multilayer films

Study on microstructure and interdiffusion behavior in Pb(FeNb)O3/Pt/Ti/SiO2/Si(100) multilayer films

The diffusion behavior of Pt/Ti electrode and its effect on ferroelectric thin films

Investigation of microstructure evolution in Pt-doped TiO2 thin films deposited by rf magnetron sputtering

Formation of Pb0.6sr0.4(Ti0.97mg0.03)O-2.97 Thin Films on Assembled Bottom Electrodes with Titanium Silicide Nanowires

Effect of Finite Interfacial Diffusion on Microstructure, Magnetic Properties and Hardness of FePt/B4C Multilayer Thin Films

Investigation on the microstructure and magnetic properties of FePt films prepared by sequentially sputtering

Effect of Pt film thickness on PtSi formation and film surface morphology

Effect of TiO_2 Seed Layer on 0.7Pb(mg_(0.33)nb_(0.67))o_3-0.3Pbtio_3 Thin Films Deposited by Radio Frequency Magnetron Sputtering

Study of the Micro-Structure of Ptxsi Ultra-Thin Film

Microstructure Transformation and Interface Structure of Co/Pt Nano-Multilayers Prepared by Ion Beam Sputtering Deposition (IBSD)

The Diffusion Mechanism of Fe-Pd Films Deposited on Ta1

High-Resolution X-Ray Reflectivity Study of Thin Layered Pt-Electrodes for Integrated Ferroelectric Devices

Fabrication of Lead Iron Niobate Films on Si Substrate by Pulsed Laser Deposition

Microstructure of Fe/Pt film anneled in magnetic field

Influence of Ti Interlayer on Untrathin Ni Film Silicidation

Preparation of platinum silicide films by pulsed laser deposition and pulsed laser annealing

Microstructural evolution of Fe/Ti multilayers submitted to in situ thermal annealing

Microstructure and magnetic properties of FeRh thin films with Pt doping

Microstructure and Magnetic Properties of (001)-Oriented L10 FePt Films: Role of Ag Underlayer and Fe/Pt Ratio

Microstructure and magnetic properties of (0 0 1)-oriented L1 0 FePt films: Role of Ag underlayer and Fe/Pt ratio