Abstract:Tantalum is used as a diffusion barrier and adhesion promoter layer between the dielectric material and copper interconnects. The present study was intended to investigate the effect of oxidizer and solution pH on chemical mechanical planarization of tantalum. High purity Ta disks were used to study the dissolution and oxidation kinetics under static and dynamic conditions using various solutions in acidic and alkaline pH regimes. The electrochemical measurements during dynamic polishing of a Ta disk were carried out using slurries containing silica and alumina particles with hydrogen peroxide at various pH levels. The affected surface layers of the statically etched Ta disk were investigated using X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM), and secondary ion mass spectrometry (SIMS). Ta metal was observed to oxidize in aqueous solutions at pH 2, 4, and 12 in absence of The oxidation process follows the parabolic kinetic law and oxidation rate was observed to be higher in an alkaline region than in an acidic region. In the presence of however, Ta dissolved in the alkaline region. The dissolution was found to be greater at pH 12 mainly because of enhanced dissociation of in alkaline region. At pH 2, on the contrary, mass gain was observed probably due to an increase in content on the top of Ta oxide formed on the surface as confirmed by XPS and SIMS depth profile studies. XPS study revealed that the oxidation of tantalum takes place at a rapid rate and forms soluble oxotantalate and hydroxotantalate in solution at pH 12 in the presence of hydrogen peroxide. AFM study validates both the XPS and the SIMS results, indicating formation of a thin impervious oxide layer on Ta in a solution at pH 2 with 5% and a porous layer was formed on Ta in solution with 5% at pH 12. Consequently, the dissolution rate in alkaline region was enhanced which was confirmed by dynamic removal rate measurements, electrochemistry, and XPS studies. © 2002 The Electrochemical Society. All rights reserved.

Displacement Activation of Tantalum Diffusion Barrier Layer for Electroless Copper Deposition

Sn/Pd Catalyzation and Electroless Cu Deposition on TaN Diffusion Barrier Layers

Effect of ultrasonic on electroless copper deposition on Ta/SiO2/Si substrate by displacement activation method

Electroless Cu Deposition Process on TiN for ULSI Interconnect Fabrication Via Pd/Sn Colloid Activation

Atomic-Scale Observation on the Nucleation and Growth of Displacement-Activated Palladium Catalysts and Electroless Copper Plating

Direct, Sequential Growth of Copper Film on TaN/Ta Barrier Substrates by Alternation of Pb-UPD and Cu-SLRR

Electroless Cu Deposition on a TiN Barrier in CuSO[sub 4]-HF Solution

Electroless Deposition of Pure Co on TaN Substrate for Interconnect Metallization

Displacement Reactions Between Metal Ions and Nitride Barrier Layer/Silicon Substrate

Tan/Ta As an Effective Diffusion Barrier for Direct Contact of Copper and Nisi

Interface Reaction of SiO2/Ta and Its Influence on Cu Diffusion

Pd Nanoparticles As a New Activator for Electroless Copper Deposition

Acidic Electroless Cu Deposition in Cuso4-Nh4f Solution

Effect of Ph and H[sub 2]o[sub 2] on Ta Chemical Mechanical Planarization

Electrodeposition of Cu on CoTa Barrier in the Alkaline CuSO4-Ethylenediamine Solution

Electroless Copper Deposition for Ultralarge-Scale Integration

Atomic layer deposition of amorphous Ni-Ta-N films for Cu diffusion barrier

Electroless Ni–Mo–P Diffusion Barriers with Pd-activated Self-Assembled Monolayer on SiO2

Possibility Of Direct Electrochemical Copper Deposition Without Seedlayer

Plasma‐Enhanced Atomic Layer Deposition of Amorphous Tantalum Thin Films for Copper Interconnects Using an Organometallic Precursor

Reaction of the SiO2/Ta Interface and Its Influence on Cu Diffusion