Abstract:This study aimed to enhance the sinterability and conductivity of yttria fully stabilized zirconia electrolyte through co-doping by 2 mol% of ZnO and different contents of MnO 2 (0, 0.5, 1, 1.5 mol%) at two sintering temperatures of 1300 and 1400 °C. Phase composition identification, density, microstructure, and conductivity of the samples were evaluated using X-ray diffraction (XRD), Archimedes' method, field emission scanning electron microscopy (FESEM), and electrochemical impedance spectroscopy (EIS), respectively. The XRD results revealed that ZnO and MnO 2 are successfully doped in the fluorite structure of YSZ sintered at 1400 °C, and the cubic structure is completely preserved. However, at a sintering temperature of 1300 °C, the (111) peaks of doped samples were slightly split, which implied a slight phase transformation of YSZ from cubic to a tetragonal structure. The co-doped samples, at both sintering temperatures, showed higher relative density and grain size compared with pure YSZ. The addition of 2 mol% of ZnO and 0.5 mol% of MnO 2 at 1400 °C increased the relative density of YSZ from 81.6% to 95.1%. The increase in relative density and grain size, while maintaining the cubic structure, caused an increase in the conductivity of the mentioned sample. Compared with pure YSZ, the sample's total conductivity increased from 7.37 to 10.03 S m −1 at 800 °C. The proposed composition showed better sintering behavior, lower activation energy of grain conductivity, and higher conductivity than pure YSZ. This behavior is thought to be due to the facilitating rearrangement of atoms during sintering and an increase in oxygen ion vacancy concentration due to co-doping with the appropriate amount of ZnO and MnO 2 .

Characterization of YSZ electrolyte membrane tubes prepared by a vacuum casting method

Study on Preparation and Properties of YSZ Electrolyte Membrane Tubes with Low Cost

Sintering and Electrical Properties of YSZ Electrolyte Tubes with Thin Wall Prepared by an Improved Slip Casting

Preparation of YSZ Electrolyte Membrane Tube by Vacuum Casting and Its Application to Solid Oxide Fuel Cells

Electrical Properties of Thin-Walled 8 Mol% Yttria-Stabilized Zirconia Electrolyte Tubes Prepared by an Improved Slip Casting Method

Preparation and application of electrolyte membrane tube

Electrical Properties and Applications of （zro2）0.92 （Y2O3）0.08 Electrolyte Thin Wall Tubes Prepared by Improved Slip Casting Method

Preparation of Tubular YSZ Electrolyte and Its Application in Solid Oxide Fuel Cells

Study on the properties of YSZ electrolyte fabricated by plaster casting method

Properties of YSZ Electrolyte Sintered at 1250°C

Study on the Properties of Ysz Electrolyte Made by Plaster Casting Method and the Applications in Solid Oxide Fuel Cells

Preparation and Characterization of YSZ Porous Ceramic Tubes with a High Porosity by Wet Method

Dense YSZ Laminates Obtained by Aqueous Tape Casting and Calendering

Dense YSZ electrolyte films prepared by modified electrostatic powder coating

The Properties of YSZ Electrolyte Sintering at 1300 °C

The Propertied Of Ysz Electrolyte Sintering At 1300 Degrees Enc

A Novel Way to Fabricate Highly Porous Fibrous YSZ Ceramics with Improved Thermal and Mechanical Properties

Influence of Solid Loading in the Gel-Casting Process on the Microstructure and Properties of Porous YSZ Ceramics

Study on Isostatic Pressing Ysz Membranes Fabricated by Tape Casting

Enhancing sintering behavior and conductivity of YSZ electrolyte by co-doping of ZnO and MnO 2

Effects of ZnO Sintering Additive on the Sintering Behavior and Conductivity of YSZ Solid Electrolyte