Abstract:Homogenously doped and mixed yttria stabilized zirconia, YSZ (with 3 and 10mol% Y2O3 known as 3YSZ and 10YSZ) and NiO/10YSZ co-precipitates (nominally corresponding to 7, 12, 24, 30, 35 and 45vol.% Ni metal), were synthesized using a continuous hydrothermal flow synthesis (CHFS) system which uses a stream of superheated water at 450°C and 24.1MPa as a reaction medium to cause rapid precipitation of metal oxide nanoparticle co-precipitates from a mixed metal salt solution. All products were obtained directly from the outlet of the CHFS reactor as a slurry, which was then cleaned and freeze-dried prior to further processing. The highly crystalline nano-powdered products were characterized using a range of analytical methods, including: powder X-ray diffraction (XRD), energy dispersive spectroscopy (EDS), transmission electron microscopy (TEM), Raman spectroscopy and BET surface area measurements. Spherical primary particles of 10YSZ and 3YSZ were observed under the TEM and found to be 5.0±0.8nm (range 3.2–6.3nm) and 6.2±1.4nm (range 3.3–8.4nm) in size, with measured BET surface areas of 160.6 and 241.7m2g−1, respectively. Sintering of the nano-powder co-precipitates was performed via spark plasma sintering (SPS) at 1100°C for 1min, leading to densities of ca. 98% for 10YSZ and ca. 96% for Ni/10YSZ cermets (all NiO was converted into Ni due to the reducing atmosphere of the SPS). The 24% Ni/10YSZ cermet was subjected to focused ion beam tomography, which allowed the 3D arrangement of the conducting Ni metallic network of the dense cermet to be elucidated, and showed that a complete 3D network of Ni existed throughout the dense cermet disk. Electrical conductivity tests showed that the samples exhibited higher than expected electrical conductivity (for such low metal content), e.g., the 24vol.% Ni-containing sample achieved an electrical conductivity of ∼200Scm−1 at the fuel cell operating temperature, which corresponds to an effective conductivity of ∼117Scm−1 if a porosity of 30% were to be introduced.

Properties of YSZ Electrolyte Sintered at 1250°C

YSZ Thin Films Prepared by a Novel Powder Coating Process on Porous NiO-YSZ Cermet

The Properties of YSZ Electrolyte Sintering at 1300 °C

The Propertied Of Ysz Electrolyte Sintering At 1300 Degrees Enc

Cubic Yttria Stabilized Zirconia Sintering Additive Impacts: A Comparative Study

Properties of YSZ Electrolyte Thin Film by Tape Calendering Process

Research on Sintering Process of YSZ Electrolyte

Synthesis of YSZ film by solid single source PE-MOCVD method and characterization

Relation Between Powder Size and Electrolyte Properties in Nano Ysz System

Fabrication, Microstructure and Properties of A Ysz Electrolyte for Sofcs

Fabrication and Characterizations of Ysz Electrolyte Films for Sofc

Enhancing sintering behavior and conductivity of YSZ electrolyte by co-doping of ZnO and MnO 2

Highly conductive low nickel content nano-composite dense cermets from nano-powders made via a continuous hydrothermal synthesis route

Dense YSZ electrolyte films prepared by modified electrostatic powder coating

Grain characters and sintering properties of YSZ nanocrystalline powders

Preparation of Bi2O3-YSZ and YSB-YSZ Composite Powders by a Microemulsion Method and Their Performance as Electrolytes in a Solid Oxide Fuel Cell

Preparation and Electrochemical Behavior of Dense Ysz Film for Soec

Fabrication of Pure T′ Phase YSZ Ceramics by Spark Plasma Sintering

Annealing temperature induced improved crystallinity of YSZ thin film

Effect of Li2o Additions Upon the Crystal Structure, Sinterability and Electrical Properties of Yttria Stabilized Zirconia Electrolyte

Influence of Thickness on the Electrical Conductivity of YSZ Electrolytes