Abstract:This study aimed to enhance the sinterability and conductivity of yttria fully stabilized zirconia electrolyte through co-doping by 2 mol% of ZnO and different contents of MnO 2 (0, 0.5, 1, 1.5 mol%) at two sintering temperatures of 1300 and 1400 °C. Phase composition identification, density, microstructure, and conductivity of the samples were evaluated using X-ray diffraction (XRD), Archimedes' method, field emission scanning electron microscopy (FESEM), and electrochemical impedance spectroscopy (EIS), respectively. The XRD results revealed that ZnO and MnO 2 are successfully doped in the fluorite structure of YSZ sintered at 1400 °C, and the cubic structure is completely preserved. However, at a sintering temperature of 1300 °C, the (111) peaks of doped samples were slightly split, which implied a slight phase transformation of YSZ from cubic to a tetragonal structure. The co-doped samples, at both sintering temperatures, showed higher relative density and grain size compared with pure YSZ. The addition of 2 mol% of ZnO and 0.5 mol% of MnO 2 at 1400 °C increased the relative density of YSZ from 81.6% to 95.1%. The increase in relative density and grain size, while maintaining the cubic structure, caused an increase in the conductivity of the mentioned sample. Compared with pure YSZ, the sample's total conductivity increased from 7.37 to 10.03 S m −1 at 800 °C. The proposed composition showed better sintering behavior, lower activation energy of grain conductivity, and higher conductivity than pure YSZ. This behavior is thought to be due to the facilitating rearrangement of atoms during sintering and an increase in oxygen ion vacancy concentration due to co-doping with the appropriate amount of ZnO and MnO 2 .

Relation Between Powder Size and Electrolyte Properties in Nano Ysz System

Influence of Thickness on the Electrical Conductivity of YSZ Electrolytes

The Propertied Of Ysz Electrolyte Sintering At 1300 Degrees Enc

The Properties of YSZ Electrolyte Sintering at 1300 °C

Preparation and Electronic Properties of Nanometer YSZ

Properties of YSZ Electrolyte Sintered at 1250°C

Fabrication, Microstructure and Properties of A Ysz Electrolyte for Sofcs

Study on the properties of YSZ electrolyte fabricated by plaster casting method

Nano-dispersed yttria-stabilized zirconia powder: Phase, morphology, and conductivity investigation with different chelating agents via a modified sol-gel method

Ionic Conductivity and Its Temperature Dependence of Atmospheric Plasma-Sprayed Yttria Stabilized Zirconia Electrolyte

Enhancing sintering behavior and conductivity of YSZ electrolyte by co-doping of ZnO and MnO 2

Preparation and Electrical Properties Test of Yttria Stabilized Zirconia

Ionic Conductivity of Electrolytes Composed of Oleate-Capped Yttria-Stabilized Zirconia Nanoparticles

Simple Preparation of Yttria‐Stabilized Zirconia Powders by Plasma Discharge Electrolysis in Nitrate Solution

Grain characters and sintering properties of YSZ nanocrystalline powders

Study on the Properties of Ysz Electrolyte Made by Plaster Casting Method and the Applications in Solid Oxide Fuel Cells

Research on Sintering Process of YSZ Electrolyte

Theoretical Study on the Influence of the Anharmonic Effect on the Ionic Conductivity and Thermal Stability of 8 mol% Yttria-Stabilized Zirconia Solid Electrolyte Material

Influence of Bi<sub>2</sub>O<sub>3</sub> on Microstructure and Properties of YSZ Solid Electrolyte Material

Electrical Properties of Thin-Walled 8 Mol% Yttria-Stabilized Zirconia Electrolyte Tubes Prepared by an Improved Slip Casting Method

Study on the properties of Al2O3-doped (ZrO2)0.92(Y2O3)0.08 electrolyte