Properties of Yttria Doped Zirconia Electrolyte with Li2O Additive

韩敏芳,焦成冉,熊洁

DOI: https://doi.org/10.14062/j.issn.0454-5648.2012.10.007

2012-01-01

Abstract:The zirconia doped with yttria of 8%(mole fraction,the same below)(8YSZ) is a widely used electrolyte in solid oxide fuel cells(SOFCs).The crystal structure,lattice parameter,sintering ability,microstructure,conductivity and cell performance of 8YSZ with various Li2O contents(i.e.,n% of Li2OYSZ,where n = 0,0.25,0.50,1.00,1.50,1.70,2.00,2.50 and 3.00) were investigated.The results show that the lithium ions can dissolve into the ZrO2cubic lattice and reduce its lattice parameter due to small radius of lithium ions.The YSZ remained its cubic lattice until Li2O addition of 1.70%.Li2O addition of 0.25% and 0.50% enhanced both the density and electrical conductivity of the YSZ samples.The conductivities obtained at Li2OYSZ of 0.25% and 0.50% and 800 ℃ were 0.030 2 S/cm and 0.027 6 S/cm,which were 1.35 and 1.24 times greater than that of pure YSZ,respectively.The density of the YSZ samples reduced gradually when the Li2O addition was greater than 1.00%.The dense ceramic with the pure cubic phase could be obtained at sintering temperature of 〉 1 400 ℃ and Li2OYSZ of ≥1.70%.The SOFCs with Li2OYSZ of 0.25% and 0.50% electrolyte displayed open circuit voltages of 〉 1.0 V at 800 ℃,indicating the absence of electronic conductivity,and exhibiting the maximum power densities that are greater than those of the cell with pure YSZ electrolyte.It was demonstrated that a small amount of Li2O addition into YSZ electrolyte could be a desirable modification approach for zirconia-based SOFC.