Abstract:This study aimed to enhance the sinterability and conductivity of yttria fully stabilized zirconia electrolyte through co-doping by 2 mol% of ZnO and different contents of MnO 2 (0, 0.5, 1, 1.5 mol%) at two sintering temperatures of 1300 and 1400 °C. Phase composition identification, density, microstructure, and conductivity of the samples were evaluated using X-ray diffraction (XRD), Archimedes' method, field emission scanning electron microscopy (FESEM), and electrochemical impedance spectroscopy (EIS), respectively. The XRD results revealed that ZnO and MnO 2 are successfully doped in the fluorite structure of YSZ sintered at 1400 °C, and the cubic structure is completely preserved. However, at a sintering temperature of 1300 °C, the (111) peaks of doped samples were slightly split, which implied a slight phase transformation of YSZ from cubic to a tetragonal structure. The co-doped samples, at both sintering temperatures, showed higher relative density and grain size compared with pure YSZ. The addition of 2 mol% of ZnO and 0.5 mol% of MnO 2 at 1400 °C increased the relative density of YSZ from 81.6% to 95.1%. The increase in relative density and grain size, while maintaining the cubic structure, caused an increase in the conductivity of the mentioned sample. Compared with pure YSZ, the sample's total conductivity increased from 7.37 to 10.03 S m −1 at 800 °C. The proposed composition showed better sintering behavior, lower activation energy of grain conductivity, and higher conductivity than pure YSZ. This behavior is thought to be due to the facilitating rearrangement of atoms during sintering and an increase in oxygen ion vacancy concentration due to co-doping with the appropriate amount of ZnO and MnO 2 .

Effects of ZnO Sintering Additive on the Sintering Behavior and Conductivity of YSZ Solid Electrolyte

Cubic Yttria Stabilized Zirconia Sintering Additive Impacts: A Comparative Study

Enhancing sintering behavior and conductivity of YSZ electrolyte by co-doping of ZnO and MnO 2

Effect of Li2o Additions Upon the Crystal Structure, Sinterability and Electrical Properties of Yttria Stabilized Zirconia Electrolyte

The Properties of YSZ Electrolyte Sintering at 1300 °C

Properties of Yttria Doped Zirconia Electrolyte with Li2O Additive

The Propertied Of Ysz Electrolyte Sintering At 1300 Degrees Enc

Preparation of Bi2O3-YSZ and YSB-YSZ Composite Powders by a Microemulsion Method and Their Performance as Electrolytes in a Solid Oxide Fuel Cell

Sintering and Electrical Conductivity of the GdSmZr2O7 Ceramic with and Without ZnO Sintering Aid

Influence of Triple Sintering Additives (Bao-Cuo-b2o3) on the Sintering Behavior and Conductivity of the Proton-Conducting BaZr0.1Ce0.7Y0.2O3−δ Electrolyte Sintered at 1150 °C

Influence of ZnO Additive on the Properties of Y-doped BaSnO3 Proton Conductor

Study on the Properties of Ysz Electrolyte Made by Plaster Casting Method and the Applications in Solid Oxide Fuel Cells

Study on the properties of Al2O3-doped (ZrO2)0.92(Y2O3)0.08 electrolyte

Sintering behavior and conductivity study of yttrium-doped BaCeO 3-BaZrO3 solid solutions using ZnO additives

Controlled Synthesis of Bi2O3-YSZ Composite Powders and Their Sintering Behavior for High-Performance Electrolytes

Effect of Two Different ZnO Addition Strategies on the Sinterability and Conductivity of the BaZr0.4Ce0.4Y0.2O3−δ Proton-Conducting Ceramic Electrolyte

Sintering and Electrical Properties of YSZ Electrolyte Tubes with Thin Wall Prepared by an Improved Slip Casting

Effects of Aluminum Oxide Addition on Electrical and Mechanical Properties of 3 mol% Yttria-Stabilized Tetragonal Zirconia Electrolyte for IT-SOFCs

The Effect of Fe Doping on the Properties of SOFC Electrolyte YSZ

Effect Of Sio2 Content On Sintering Characteristics Of Ysz In High Temperature Aging

Influence of Bi<sub>2</sub>O<sub>3</sub> on Microstructure and Properties of YSZ Solid Electrolyte Material