Effect of Two Different ZnO Addition Strategies on the Sinterability and Conductivity of the BaZr0.4Ce0.4Y0.2O3−δ Proton-Conducting Ceramic Electrolyte

Zhen Wang,Luyao Ding,Shenglong Yu,Huan Xu,Xiaohui Hao,Yi Sun,Tianmin He
DOI: https://doi.org/10.1021/acsaem.1c03989
IF: 6.4
2022-01-01
ACS Applied Energy Materials
Abstract:A comparative study has been made to relate the effect of different addition strategies for the sintering aid of ZnO (similar to 1 wt %) on the performance of the BaZr0.4Ce0.4Y0.2O3-delta (BZCY442) electrolyte in order to improve the sinterability and conductivity of this material more efficiently. Two samples, Zn-doped BaZr(0.4)Zr(0.4)Y(0.15)Z(3-delta) (BZCYZn, internal doping) and BZCY-ZnO (BZCY442 mixed with ZnO, external addition), were synthesized. The BZCYZn crystallized at a single phase after sintering at 1350 degrees C, and the segregation of Y2O3 was observed in BZCY-ZnO in the same conditions. The relative densities of the BZCYZn and BZCY-ZnO samples sintered at 1350 degrees C for 5 h were 98 and 94%, respectively. The high total conductivity in BZCYZn benefited from the low barrier height at the grain boundary core determined by the Mott-Schottky space charge layer model, which was 0.15 V for BZCYZn and 0.26 V for BZCY-ZnO. A cell with BZCYZn as the electrolyte generated a power density of 414.5 mW cm(-2) at 700 degrees C. The total ionic transport number of BZCYZn was determined to be similar to 0.90 at 600 degrees C under fuel cell conditions.
What problem does this paper attempt to address?