Abstract:Aiming at the high temperature corrosion problem of the water wall of a 350 MW low nitrogen boiler in a power plant, the simulation study was carried out to adjust the air distribution and increasing near-wall air. The relationship between the concentration of reducing gases CO, H 2 S and NO x in the furnace was simulated when the burn-out air rate was 38%, 33% and 27% respectively, and the effect of increasing the wall air on the concentration of reducing gases near the water wall was simulated. The results show that the burn-out air rate is reduced from 38% to 33%, which can reduce the concentration of reducing gases CO and H 2 S in the furnace by 20% without significantly increasing the amount of NO x , and slow down the high-temperature corrosion of the water wall. Reducing the burn-out air rate from 38% to 27% can increase the oxygen concentration in the main combustion zone, reduce the production of CO and H 2 S, and slow down the high-temperature corrosion of the water wall, but the NO x concentration will increase significantly. The high-temperature corrosion area in the furnace is mainly located between the UAP nozzle of the compact burnout air and the SOFA3 nozzle of the intermediate burnout air. The near-wall air can be added on both sides of the UAP nozzle of the compact burnout air. The simulation results show that the concentration of CO and H 2 S near the water wall can be reduced by increasing the near-wall wind with the same rotation direction as the main flow, and there is the small effect on the flow field. Due to the high concentration of CO near the water wall, the flow of near-wall air on both sides is larger, which has better effect on reducing CO near the water wall. The coverage area of near-wall air on both sides is larger for high-temperature corrosion area, while the concentration of H 2 S near the water wall is lower. There is no obvious difference between the single-side near-wall air and the double-side near-wall air in reducing the H 2 S of the water wall, but the double-side near-wall air will disturb the distribution of the flow field, which is not conducive to pulverized coal combustion.

Water Wall of Pulverized Coal Fired Boiler's Scaling Erosion and its Reasons

Experimental Investigation of the Scaling-Off Location and the Slag Mass in Pulverized Coal-Fired Boiler with Water-Cooled Slag Removal

Effect of metal anti-wear device on the water wall erosion in CFB boiler

Water Wall Tubes’ High Temperature Corrosion Root Cause Investigation: A 300 MW Level Boiler Case

Application of Multi-Tangential Firing Technology to Settling the High Temperature Corrosion of Water Wall Tube of Boiler

Metal Anti-wear Device Structure Optimization Design and Application in CFB Boiler

Leakage of water-cooled wall tube in subcritical boiler

Cause and mechanism analysis of cracking and leakage of water wall tube

Analysis and Solution of High-temperature Corrosion for a 1000 MW Ultra-supercritical Boiler

Effect of burnout air rate and wall air on high temperature corrosion of water wall of 350 MW tangentially fired boiler

Numerical investigation of boiler waterwall corrosion by integrated tube temperature prediction and sulfur evolution model

Numerical study of solid particle erosion on sidewall

Application study on enamel heat exchange tube in GGH of coal-fired units with ultra-low flue gas emission

High-temperature corrosion of water-wall tubes in oxy-combustion atmosphere

Failure Analysis on Corrosion of Refeed Valve Manhole Door in Circulating Fluidized Bed Boiler

Investigation on slagging and high-temperature corrosion prevention and control of a 1000 MW ultra supercritical double tangentially fired boiler

The hydrodynamic characteristics of embattlement shaped water wall of a 350 mw supercritical circulating fluidized bed boiler

Development of the Design of a 600 MW Low Mass Flow Speed Supercritical Pulverized Coal-fired Boiler with a Vertical Tube Coil

Safety Evaluation on Corrosion and Abrasion Situation of CFB Boiler System

An Effective Strategy for Monitoring Slagging Location and Severity on the Waterwall Surface in Operation Coal-Fired Boilers

Corrosion Evaluation of One Dry Desulfurization Equipment - Circulating Fluidized Bed Boiler