Analysis and Solution of High-temperature Corrosion for a 1000 MW Ultra-supercritical Boiler

Hongkun Lü,Jialin TONG,Jianzhong LIU,Ming ZHANG,Jianguo XIONG,Zhijun ZHOU

DOI: https://doi.org/10.11936/bjutxb2016070021

2017-01-01

Abstract:In order to control the high-temperature corrosion of water-wall, the pinning atmosphere was measured and the flake pieces were analyzed by SEM, EDS and XRD. The results show that the main reasons of water-wall high-temperature corrosion are cycle-by-cycle variation of reductive atmosphere. The area of most intense of reductive atmosphere and the concentration of H2 S is between OFA and SOFA. The possibility of the high-temperature corrosion of this area is great. Dual tangential circle wall firing can raise the concentration of H2 S at front-wall and back-wall. The outside corrosion product is Fe2 O3 , and on the contrary, the inside one is FeS. The alternation of the pinning atmospheres from oxidation atmosphere to reductive atmosphere which caused by load was a key factor of the high-temperature corrosion. In actual operation of boiler, optimizing air distribution mode and keeping the pinning atmosphere stabilization can reduce the rate of the high-temperature corrosion to low NOx combustion boilers.