Abstract:Many nanoporous Si structures, including those formed by common electrochemical etching procedures, produce a uniformly etched nanoporous surface. If the electrochemical etch rate is slowed down, details of the etch process can be explored and process parameters may be varied to test hypotheses and obtain controlled nanoporous and defect structures. For example, after electrochemical etching of heavily n-doped (R = 0.05-0.5 Omega.cm) silicon (100 single crystals at a current density of 10 mA cm(-2) in buffer oxide etch (BOE) electrolyte solution, defect craters containing textured nanopores were observed to occur in ring-shaped patterns. The defect craters apparently originate at the hydrogen/BOE bubble interface, which forms during hydrogen evolution in the reaction. The slower hydrogen evolution due to low current density and high BOE viscosity allows sufficient bubble residence time so that a high defect density appears at the bubble edges where local reaction rates are highest. Current-carrying Si-OH species are most likely responsible for the widening of the craters. Reducing the defect/doping density in silicon lowers the defect concentration and thereby the density of nanopores. Measurements of photoluminescence lifetime and intensity show a distinct feature when the few nanopores formed at the ring edges are isolated from each other. Overall features observed in the photoluminescence intensity by XPS strongly emphasize the role of surface oxide that influences these properties. Copyright (c) 2005 John Wiley & Sons, Ltd.

Hydrofluoric Acid Free Synthesis of Macropores on Silicon by Chemical Vapor Deposition and Their Photoluminescence

Photoluminescence, Composition and Microstructure of Porous Silicon Prepared by Different Substrates

Precise Fabrication of Point Defects in Self-Assembled Three-Dimensional Macroporous Photonic Crystals.

On the Role of the Pore Filling Medium in Photoluminescence from Photochemically Etched Porous Silicon

Hydrogen Bubbles and Formation of Nanoporous Silicon During Electrochemical Etching

Preparation and Characterization of Free-Standing Porous Silicon Films with High Porosity

Preparation and Photoluminescence of Nanocrystalline Si-Rich Silicon Oxide Films by Pecvd

Preparation Of Porous Silicon Using Anodizing And Suppercritical Drying

Pulsed Anodic Etching: an Effective Method of Preparing Light-Emitting Porous Silicon

A novel method of fabricating porous silicon material: ultrasonically enhanced anodic electrochemical etching

Atomic Force Microscopic Studies of Light-Emitting Porous Silicon

Hierarchical Nanostructuring of Porous Silicon with Electrochemical and Regenerative Electroless Etching

Studies on microstructure and photoluminescence property of porous silicon

Flat Layered Structure and Improved Photoluminescence Emission from Porous Silicon Microcavities Formed by Pulsed Anodic Etching

Remote and Rapid Micromachining of Broadband Low-Reflectivity Black Silicon Surfaces by Femtosecond Laser Filaments.

Dimensional Constraints on High Aspect Ratio Silicon Microstructures Fabricated by HF Photoelectrochemical Etching

Photo-electrochemical Etching of Macroporous Silicon Arrays Used in Silicon Microchannel Plates

Narrow-Line Light Emission from Porous Silicon Multilayers and Microcavities

Nanoscale Silicon Prepared on Different Substrates Using Electron-Beam Evaporation and Their Field-Emission Property

Photoluminescence from Silicon nanoparticles embedded in ammonium silicon hexafluoride

Experimental Study on Evolution of Chemical Structure Defects and Secondary Contaminative Deposition during HF-Based Etching