Preparation Of Nanosized Nio-Ysz Composite Powders By Situ-Precipitation Method

Liang Mingde,Yu Bo,Wen Mingfen,Zhai Yuchun

DOI: https://doi.org/10.3321/j.issn:1002-185X.2009.z2.119

2009-01-01

Rare Metal Materials and Engineering

Abstract:Nickel oxide and yttria-stabilized zirconia (NiO-YSZ) composite powders were synthesized by situ-precipitation method to prepare high performance hydrogen electrode with long-term durability operating in the Solid Oxide Electrolysis Cells (SOEC) mode. The products were characterized by XRD and FESEM, and the effect of pH on the average crystallite size and yield of the NiO was studied. A single SOEC with 500 mu m NiO-YSZ support, 20 mu m NiO-YSZ interlayer, 10 mu m NiO-YSZ hydrogen electrode, 4 mu m YSZ electrolyte, 6 mu m SDC electrolyte and 20 mu m BSCF oxygen electrode was prepared for performance tests. The results showed that the NiO-YSZ composite powders agglomerate to form spongy structure and the optimized pH of NiO-YSZ synthesized was 8.5. The related NiO average crystallite size is 13 nm and the yield is 94.5%. When the steam content in the input stream is 70%, 80% and 90% at 850 degrees C, the hydrogen production rate of the single SOEC is 266, 381 and 558 N.mL/cm(2).h, respectively. The electrolytic voltage changed from 1.09 to 1.16 Vat 1 h before and after the electrolysis with the current density of 0.33 A/cm(2) at 850 degrees C and 90% H2O + 10% H-2 as inlet gas, which showed the prepared SOEC had excellent durability.