Abstract:New Cu-based bulk glassy alloys were formed in Cu–Zr–Ti and Cu–Hf–Ti systems by the copper mold casting method. The critical diameter is 4 mm for the Cu60Zr30Ti10 and Cu60Hf25Ti15 alloys which are larger than 1 mm for the Cu60Zr40 and Cu60Hf40 glassy alloys. The substitution of Zr or Hf for Ti causes an increase in the glass-forming ability (GFA). As the Ti content increases, the glass transition temperature (Tg), crystallization temperature (Tx), and the supercooled liquid region ΔTx(=Tx−Tg) decrease for both Cu60Zr40−xTix and Cu60Hf40−xTix alloys. In contrast, the liquid temperature (Tl) has a minimum value of 1127 K for the Cu60Zr20Ti20 alloy and 1175 K for the Cu60Hf20Ti20 alloy, resulting in a maximum Tg/Tl of 0.63 and 0.62, respectively. The alloys with the highest Tg/Tl value showed the highest GFA for these Cu-based alloys. The bulk glassy alloys exhibit high tensile fracture strength of 2000–2160 MPa, compressive fracture strength of 2060–2150 MPa and compressive plastic elongations of 0.8–1.7%. The finding of the new Cu-based bulk glassy alloys with high GFA, high fracture strength above 2000 MPa and distinct plastic elongation is encouraging for the future development of a new type of bulk glassy alloy which can be used for structural materials.

A New Ti–Zr–Hf–Cu–Ni–Si–Sn Bulk Amorphous Alloy with High Glass-Forming Ability

Effect of Sn addition on the glass-forming ability in (Cu40Ti30Ni15Zr10)(100-x)/95Snx (x = 0, 2, 4, 6 and 8) alloys

Preparation of (ti0.45cu0.378zr0.10ni0.072)100−xsnx Bulk Metallic Glasses

Formation and Compressive Properties of A Ni-Ti-Zr-Al-Cu-Si Amorphous Alloy

Effect of Minor Sn Additions on the Formation and Properties of TiCuZrPd Bulk Glassy Alloy

Enhancing bulk metallic glass formation in Ni–Nb–Sn-based alloys via substitutional alloying with Co and Hf

A Ti-based bulk glassy alloy with high strength and good glass forming ability

Crystallization and mechanical behavior of (Hf, Zr)–Ti–Cu–Ni–Al metallic glasses

Effect of Sn addition on thermal stability of (Zr52.5Ti5Al10 Ni14.6Cu17.9) Sn-(100-x)(x) alloys

BULK AMORPHOUS Zr-Cu-Ni-Al-Hf-Ti ALLOYS WITH SUPERCOOLED LIQUID REGION OVER 140℃

Cu-Based Bulk Glassy Alloys with Good Mechanical Properties in Cu-Zr-Hf-Ti System

High-strength Cu-based bulk glassy alloys in Cu–Zr–Ti and Cu–Hf–Ti ternary systems

Effect of Sn addition on thermal stability of (Zr52.5Ti 5Al10Ni14.6Cu17.9) (100-x)Snx alloys

Effect of Ti addition on supercooled liquid region and glass forming ability of bulk amorphous Zr60Cu20Ni10-xAl10Tix alloys

PREPARATION AND PROPERTIES OF HIGH STRENGTH BULK METALLIC GLASS Ti_(53)Cu_(15)Ni_(18.5)Al_7M_3Si_3B_(0.5) (m=zr, Hf, Sc)

Fabrication and Soft Magnetic Properties of Fe–B–Si–Zr/Hf–Cu Nanocrystalline Alloys with High Glass-Forming Ability

EFFECT OF Ti ADDITION ON THE GLASS--FORMING ABILITY OF (Zr0.59cu0.18ni0.13al0.10)100-Xtix ALLOYS

Formation and Thermal Properties of Ti-Based Bulk Amorphous Alloy

A method locating Cu-Ti-based glass formers using Ni-Zr binary clusters

The Relations Between ΔT and the Glass Forming Ability of Bulk Amorphous Zr–Cu–Ni–Al–Hf–Ti and Zr52.5Cu17.9Ni14.6Al10Ti5 Alloys

Crystallization processes from supercooled liquid of Cu40Ti30Ni15Zr10Sn5 and Zr60Ni25Al15 amorphous alloys