Effect of Ti addition on properties of Zr54Al10.2Ni9.4Cu26.4 glass forming alloy

D.W. Ding,Jing Tan,A.H. Cai,Y. Liu,H. Wu,Q. An,P.W. Li,Yan. Zhang,Qing Yang

DOI: https://doi.org/10.1016/j.jallcom.2021.158911

IF: 6.2

2021-05-01

Journal of Alloys and Compounds

Abstract:(Zr54Al10.2Ni9.4Cu26.4)100−xTix (x = 0–0.5, at%) bulk metallic glasses were prepared by water-cooled copper suction casting method. The Ti microalloying effect on glass forming ability and physical and chemical properties of Zr54Al10.2Ni9.4Cu26.4 glass forming alloy were systematically investigated. The glass forming ability is the largest for the Zr-based alloy with 0.3 at% Ti. The glass transition temperature is decreased by the Ti addition, while the supercooled liquid region is broadened. Both strength and plasticity are significantly enhanced by the Ti addition. The yield strength and the fracture strength firstly increase and then decrease when the Ti content reaches up to 0.3 at%. The plastic strain and the fracture strain increase with increasing Ti content. In addition, the corrosion potential is slightly decreased by the Ti addition. The corrosion current density increases with increasing Ti content. The pitting corrosion becomes increasingly serious with increasing Ti content. The honeycomb corrossion structure can be clearly observed when the Ti content reaches up to 0.5 at%. The corresponding mechanisms are also discussed in detail.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The paper primarily investigates the effects of titanium (Ti) microalloying on the properties of Zr-based amorphous alloys. Specifically, the paper explores the impact of adding different amounts of titanium (x = 0–0.5 at%) to the Zr₅₄Al_10.2Ni_9.4Cu_26.4 glass-forming alloy on its glass-forming ability, thermodynamic properties, mechanical properties, and corrosion resistance.

1. **Glass-forming ability**: The study found that the alloy's glass-forming ability is strongest when the Ti content is 0.3 at%.
2. **Thermodynamic properties**: With the addition of Ti, the glass transition temperature (T_g) decreases, while the supercooled liquid region (ΔT_x) first increases and then decreases.
3. **Mechanical properties**: The addition of Ti significantly improves the alloy's strength and plasticity. The yield strength (σ_y) and fracture strength (σ_f) increase first and then decrease with the increase in Ti content; the plastic strain (ε_p) and fracture strain (ε_f) increase with the increase in Ti content.
4. **Corrosion resistance**: The addition of Ti leads to a slight decrease in corrosion potential (E_c), and the corrosion current density (i_c) increases with the increase in Ti content, with pitting corrosion becoming more severe.

Through these experimental results, the paper reveals the specific effects of Ti microalloying on the properties of Zr-based amorphous alloys and the related mechanisms.