Abstract:Bulk glassy Cu–Zr–Ti base alloys containing a small amount of Nb or Ta were found to exhibit high strength combined with significant plastic elongation. The glass transition temperature (Tg), crystallization temperature (Tx) and ΔTx(=Tx−Tg) of the Cu-based bulk glassy alloys are in the range of 719 to 731 K, 765 to 769 K and 46 to 44 K, respectively, for the Nb-containing alloy and 716 to 741 K, 752 to 780 K and 44 to 34 K, respectively, for the Ta-containing alloy. With increasing Nb or Ta content to 3 at% for the (Cu0.6Zr0.3Ti0.1)100−xMx alloys, the Young’s modulus, yield strength and compressive fracture strength increase from 114 to 121 GPa, 1785 to 2010 MPa and 2150 to 2250 MPa, respectively, and the plastic elongation shows a maximum of 1.8% at 1%Nb and 3.4% at 1%Ta. The 1%Ta alloy exhibited good combination of high fracture strength of 2250 MPa and large total elongation of 5.4%. The effectiveness of additional Nb or Ta on the increase in elongation and fracture strength is presumably due to the mixed state of atomic pairs with attractive and repulsive bonding natures among the constituent elements with significantly different atomic size mismatches. The success of forming the bulk glassy alloys with high strength and significant elongation is encouraging for future applications as high-strength type materials.

High-strength Cu-based bulk glassy alloys in Cu–Zr–Ti and Cu–Hf–Ti ternary systems

Cu-Based Bulk Glassy Alloys with Good Mechanical Properties in Cu-Zr-Hf-Ti System

Cu-based bulk glassy alloys with high tensile strength of over 2000 MPa

Centimeter-sized Ti-based Bulk Metallic Glass with High Specific Strength

A Ti-based bulk glassy alloy with high strength and good glass forming ability

A Ti–Zr–Be–Fe–Cu Bulk Metallic Glass with Superior Glass-Forming Ability and High Specific Strength

Glass-Forming Ability and Mechanical Properties of the Ternary Cu-Zr-Al and Quaternary Cu-Zr-Al-Ag Bulk Metallic Glasses

Formation and mechanical properties of bulk Cu-Ti-Zr-Ni metallic glasses with high glass forming ability

Thermal Stability and Mechanical Properties of Bulk Glassy Cu-Zr-Ti-(Nb, Ta) Alloys

PREPARATION AND PROPERTIES OF HIGH STRENGTH BULK METALLIC GLASS Ti_(53)Cu_(15)Ni_(18.5)Al_7M_3Si_3B_(0.5) (m=zr, Hf, Sc)

Synthesis,structure and Mechanical Properties of Zr-Cu-based Bulk Metallic Glass Composites

Formation, Thermal Stability and Mechanical Properties of Ti42.5Zr7.5Cu40Ni5Sn5 Bulk Metallic Glass

Crystallization and mechanical behavior of (Hf, Zr)–Ti–Cu–Ni–Al metallic glasses

Composition design and mechanical properties of ternary Cu–Zr–Ti bulk metallic glasses

Glass-forming Ability and Thermal Stability of a New Bulk Metallic Glass in the Quaternary Zr–Cu–Ni–Al System

Formation, Structure, and Crystallization Behavior of Cu-Based Bulk Glass-Forming Alloys

Fabrication Of Bulk Glassy Hf50cu30ni10al10 Alloy By Copper Mold Casting

A New Centimeter‐Sized Ti‐Based Quaternary Bulk Metallic Glass with Good Mechanical Properties

A New Cu–Hf–Al Ternary Bulk Metallic Glass with High Glass Forming Ability and Ductility

Failure behavior of Cu–Ti–Zr-based bulk metallic glass alloys

Ni- and Be-free Zr-based bulk metallic glasses with high glass-forming ability and unusual plasticity.