Abstract:The Ti-based bulk metallic glasses (BMG) with high Ti content (>50 at.%) have attracted wide attention for their outstanding mechanical properties, despite their glass forming ability (GFA) is still relatively poor. Here the (Ti55Zr15Be20Ni10)(100-x)Cu-x(x = 2, 4, 6, 8 and 10 at.%) BMGs were designed and prepared by copper mold casting. The critical diameter of the original alloy could be enhanced from 5 mm to 10 mm with the Cu addition of 4 at.%, which is the first reported centimeter-sized Ti-based BMG with Ti content more than 52 at.%. In addition, all the as-prepared BMGs exhibited higher yield strength (above 2000 MPa). And the supercooled liquid range of the as-prepared Ti-based BMGs were enlarged from 35 K to 74 K by Cu addition. Electrochemical measurements showed that the BMGs with Cu addition of 0-6 at.% exhibited much higher pitting potentials (over 573 mV/SCE) than that of 304 stainless steel (304SS) in 3.5 wt% NaCl aqueous solution. And The XPS analysis revealed that the Cu addition might lead to the enrichment of Cu and the deficiency of Ti, Zr, Ni elements in passive film, which could induce the worse corrosion resistance of the Ti-based BMGs with high Cu content. The results indicate that the developed Ti-based BMGs possess good GFA, mechanical properties and corrosion resistance. (C) 2017 Elsevier B.V. All rights reserved.

A Ti–Zr–Be–Fe–Cu Bulk Metallic Glass with Superior Glass-Forming Ability and High Specific Strength

Centimeter-sized Ti-based Bulk Metallic Glass with High Specific Strength

New Centimeter-Sized Quaternary Ti–Zr–Be–Cu Bulk Metallic Glasses with Large Glass Forming Ability

Centimeter-sized Ti-rich Bulk Metallic Glasses with Superior Specific Strength and Corrosion Resistance

A Centimeter-Sized Quaternary Ti-Zr-Be-Ag Bulk Metallic Glass

Lightweight Ti–Zr–Be–Al Bulk Metallic Glasses with Improved Glass-Forming Ability and Compressive Plasticity

The Novel Ti-based Metallic Glass with Excellent Glass Forming Ability and an Elastic Constant Dependent Glass Forming Criterion

Achieving ultrahigh-specific strength and enhanced GFA in Ti-based bulk metallic glasses via a two-step alloying strategy

Quaternary Ti–Zr–Be–Ni Bulk Metallic Glasses with Large Glass-Forming Ability

Ti-Zr-Be-Fe Quaternary Bulk Metallic Glasses Designed by Fe Alloying

Centimeter‐Sized Quaternary Ti‐Based Bulk Metallic Glasses with High Ti Content of 50 At%

Effects of Fe Addition on Glass-Forming Ability and Mechanical Properties of Ti–Zr–Be Bulk Metallic Glass

A Ti-based bulk glassy alloy with high strength and good glass forming ability

Effects of Cu Addition on the Glass Forming Ability and Corrosion Resistance of Ti-Zr-Be-Ni Alloys

Cu-based bulk glassy alloys with high tensile strength of over 2000 MPa

A New Centimeter‐Sized Ti‐Based Quaternary Bulk Metallic Glass with Good Mechanical Properties

High-strength Cu-based bulk glassy alloys in Cu–Zr–Ti and Cu–Hf–Ti ternary systems

Glass forming ability, thermodynamics and mechanical properties of novel Ti–Cu–Ni–Zr–Hf bulk metallic glasses

Cu-Based Bulk Glassy Alloys with Good Mechanical Properties in Cu-Zr-Hf-Ti System

The effect of minor alloying on the glass forming ability and crystallization reaction of Ti32.8Zr30.2Cu9M5.3Be22.7 (M=Fe, Co, and Ni) bulk metallic glass

CENTIMETER-SIZED Ti-BASED QUATERNARY BULK METALLIC GLASS PREPARED BY WATER QUENCHING