Abstract:Zr50Cu34-xFexAl8Ag8 (x = 0, 2, 4, 6, and 8) alloy bars of different diameters were prepared by copper mold suction casting and copper mold casting. The compressive mechanical properties of metallic glass samples with different Fe contents were determined by a universal testing machine. The microstructure and thermodynamics of the alloy samples were analyzed by X-ray diffraction, scanning electron microscopy, transmission electron microscopy, and differential scanning calorimetry. According to the experimental results, Fe doping had a significant effect on the glass-forming ability, stability, and mechanical properties of these metallic glasses. The maximum diameter of the Zr50Cu32Fe2Al8Ag8 metallic glass bar was 15 mm, and the cooling rate of the alloy sample was 7.7 K/s. The addition of Fe inhibited the formation of stable crystalline phases inside the alloy sample and improved the glass-forming ability of the metallic glass. With the addition of Fe, the DSC curve of the alloy sample moved to higher temperatures, and the characteristic temperatures and the stability of the metallic glass increased. The fracture strength (σmax) and ultimate strain (εf) of the metallic glass samples reached their maximum values of 1917.6 MPa and 3.97 %, respectively, for Zr50Cu30Fe4Al8Ag8. Compared with the Fe-free Zr50Cu34Al8Ag8 metallic glass, σmax and εf increased by 51.4 MPa and 1.19 %, respectively. With the addition of Fe, the change in the distribution and content of free volume inside the metallic glass sample is the main reason for the improvement of its mechanical properties. This study shows that trace element doping has an important effect on the properties of metallic glasses.

Ti-Zr-Be-Fe Quaternary Bulk Metallic Glasses Designed by Fe Alloying

Effects of Fe Addition on Glass-Forming Ability and Mechanical Properties of Ti–Zr–Be Bulk Metallic Glass

A Ti–Zr–Be–Fe–Cu Bulk Metallic Glass with Superior Glass-Forming Ability and High Specific Strength

Quaternary Ti–Zr–Be–Ni Bulk Metallic Glasses with Large Glass-Forming Ability

Centimeter-sized Ti-rich Bulk Metallic Glasses with Superior Specific Strength and Corrosion Resistance

Lightweight Ti–Zr–Be–Al Bulk Metallic Glasses with Improved Glass-Forming Ability and Compressive Plasticity

The effect of minor alloying on the glass forming ability and crystallization reaction of Ti32.8Zr30.2Cu9M5.3Be22.7 (M=Fe, Co, and Ni) bulk metallic glass

Achieving ultrahigh-specific strength and enhanced GFA in Ti-based bulk metallic glasses via a two-step alloying strategy

A Centimeter-Sized Quaternary Ti-Zr-Be-Ag Bulk Metallic Glass

Improved mechanical properties and corrosion resistance of Zr-Cu-Al-Ni-Ti bulk metallic glass by Fe substitution for Ni

Fe–C micro-alloying effect on properties of Zr53Al11.6Ni11.7Cu23.7 bulk metallic glass

Enhancing strength and plasticity of Zr-based bulk metallic glasses by Zr partially substituted Fe and isothermal annealing

New Centimeter-Sized Quaternary Ti–Zr–Be–Cu Bulk Metallic Glasses with Large Glass Forming Ability

Glass forming ability, thermodynamics and mechanical properties of novel Ti–Cu–Ni–Zr–Hf bulk metallic glasses

Centimeter-sized Ti-based Bulk Metallic Glass with High Specific Strength

Formation and Corrosion Properties of Fe-based Bulk Metallic Glasses

The Novel Ti-based Metallic Glass with Excellent Glass Forming Ability and an Elastic Constant Dependent Glass Forming Criterion

Centimeter‐Sized Quaternary Ti‐Based Bulk Metallic Glasses with High Ti Content of 50 At%

A Ti-based bulk glassy alloy with high strength and good glass forming ability

A novel senary Hf-Be-Ti-Zr-Cu-Ni high entropy bulk metallic glasses with high glass forming ability and high density

Effect of Fe addition on the glass-forming ability, stability, and mechanical properties of Zr50Cu34-xFexAl8Ag8 metallic glasses