Abstract:Tensile, compressive, cyclic tension-tension, and cyclic compression-compression tests at room temperature were systematically applied to a Zr52.5Cu17.9Al10Ni14.6Ti5 bulk metallic glass for comprehensive understanding of its damage and fracture mechanisms. Under tensile loading, the metallic glass only displays elastic deformation followed by brittle shear fracture. Under compressive loading, after elastic deformation, obvious plasticity (0.5 to 0.8 pct) can be observed before the final shear fracture. The fracture strength under compression is slightly higher than that under tension. The shear fracture under compression and tension does not occur along the maximum shear stress plane. This indicates that the fracture behavior of the metallic glass does not follow the Tresca criterion. The fracture surfaces show remarkably different features, i.e., a uniform vein structure (compressive fracture) and round cores coexisting with the radiating veins (tensile fracture). Under cyclic tension-tension loading, fatigue cracks are first initiated along localized shear bands on the specimen surface, then propagated along a plane basically perpendicular to the stress axis. A surface damage layer exists under cyclic compression-compression loading. However, the final failure also exhibits a pure shear fracture feature as under uniaxial compression. The cyclic compression-compression fatigue life of the metallic glass is about a factor of 10 higher than the cyclic tension-tension fatigue life at the same stress ratio. Based on these results, the damage and fracture mechanisms of the metallic glass induced by uniaxial and cyclic loading are elucidated.

Failure behavior of Cu–Ti–Zr-based bulk metallic glass alloys

Formation and mechanical properties of Cu_(58)Zr_(20)Ti_(20)Mo_2 bulk metallic glass

Formation and mechanical properties of bulk Cu-Ti-Zr-Ni metallic glasses with high glass forming ability

Stress-life fatigue behavior and fracture-surface morphology of a Cu-based bulk-metallic glass

Fatigue and fracture behavior of bulk metallic glass

Formation, Thermal Stability and Mechanical Properties of Ti42.5Zr7.5Cu40Ni5Sn5 Bulk Metallic Glass

High-strength Cu-based bulk glassy alloys in Cu–Zr–Ti and Cu–Hf–Ti ternary systems

Microstructure evolution and mechanical properties of Cu46Zr47Al7 bulk metallic glass composite containing CuZr crystallizing phases

Microstructure and Fracture Behavior of Zr55Cu30Al10Ni5 Bulk Metallic Glass and Its Composites Containing ZrO2

Cu-Based Bulk Glassy Alloys with Good Mechanical Properties in Cu-Zr-Hf-Ti System

Tension Fracture Behavior of Zr41.25ti13.75ni10cu12.5be22.5 Bulk Metallic Glass

Structure and properties of Zr–Ta–Cu–Ni–Al bulk metallic glasses and metallic glass matrix composites

Mechanical and corrosion properties of Ti-Ni-Cu-Zr metallic glass matrix composites

Fracture behavior and deformation-induced structure changes of a Ti-based metallic glass using micro-sized cantilevers

Development of High Strength Ni–Cu–Zr–Ti–Si–Sn In-Situ Bulk Metallic Glass Composites Reinforced by Hard B2 Phase

Microstructural heterogeneities governing the deformation of Cu47.5Zr47.5Al5 bulk metallic glass composites

Cu-based bulk glassy alloys with high tensile strength of over 2000 MPa

Composition design and mechanical properties of ternary Cu–Zr–Ti bulk metallic glasses

Synthesis,structure and Mechanical Properties of Zr-Cu-based Bulk Metallic Glass Composites

Pronounced Ductility in CuZrAl Ternary Bulk Metallic Glass Composites with Optimized Microstructure Through Melt Adjustment

A Ti-based bulk glassy alloy with high strength and good glass forming ability