Abstract:In this work, Cu-1.4 wt%Ta-Zr alloys with different Zr content (0, 0.1, 0.2 and 0.5 wt%) were fabricated by mechanical alloying combined with spark plasm sintering. The effect of Zr addition on the microstructures, mechanical properties and thermal stability of Cu-Ta alloy were characterized. Cu-Ta alloys composes of ultrafine equiaxed grains along with the uniformly dispersion of semi-coherent Ta nanoclusters and incoherent Ta coarse particles. As Zr is introduced into Cu-Ta alloy, the Ta precipitates were effectively refined, especially for the reduction of Ta coarse particles. The significant refinement effect of the grains is realized when Zr content reaches 0.2 wt%, and high-proportioned nano-sized grains are facilitated to form, along with the activation of a lot of twins and the formation of intermetallic composed of Cu and Zr. The dislocation density and strength increase remarkably with the increase of Zr content, and the highest strength (499 MPa for yield strength and 600 MPa for ultimate tensile strength) is achieved as the Zr content is up to 0.2 wt%. Compared with Cu-Ta alloy (382 MPa for yield strength and 560 MPa for ultimate tensile strength), the significant increment of 31% for the yield strength is successfully realized by Cu-Ta-0.2 wt%Zr alloy. Cu-Ta-0.2 wt%Zr alloys exhibit the excellent thermal stability, and the hardness keeps stable even the sample was annealed at 700 °C for 300 h, showing superior microstructural stability in comparison with Cu-Ta alloy (~4.5% reduction of the hardness after 300 h at 700 °C). The softening temperature of Cu-Ta-0.2 wt%Zr alloy is up to 1028 °C (1022 °C for Cu-Ta alloy) along with higher hardness than that of Cu-Ta alloy at the same annealing temperature. This study provides a new way to fabricate dispersion strengthened Cu alloys with high strength, exceptional thermal stability and softening resistance, which have great potential application value in the field of future fusion reactor.

Thermal Stability and Mechanical Properties of Bulk Glassy Cu-Zr-Ti-(Nb, Ta) Alloys

Effects of Small Amount Ta on the Characteristics of the Zr-Al-Ni-Cu-Ta Bulk Metallic Glass

Cu-Based Bulk Glassy Alloys with Good Mechanical Properties in Cu-Zr-Hf-Ti System

High-strength Cu-based bulk glassy alloys in Cu–Zr–Ti and Cu–Hf–Ti ternary systems

Formation, Thermal Stability and Mechanical Properties of Zr-Nb-Cu-Ni-Al Bulk Metallic Glasses

Zr-Cu-Ni-Al-Ta Glassy Matrix Composites with Enhanced Plasticity

Structure and properties of Zr–Ta–Cu–Ni–Al bulk metallic glasses and metallic glass matrix composites

Cu-based bulk glassy alloys with high tensile strength of over 2000 MPa

Tuning Glass Formation and Mechanical Properties of ZrCoAl(Nb) Bulk Metallic Glass with Nb Microalloying Process

Glass formation, corrosion behavior and mechanical properties of bulk glassy Cu–Hf–Ti–Nb alloys

Formation of Ni–Nb–Zr–X (X = Ti, Ta, Fe, Cu, Co) Bulk Metallic Glasses

Improving the glass-forming ability and plasticity of a TiCu-based bulk metallic glass composite by minor Ta doping

Ultra-high strength Co–Ta–B bulk metallic glasses: Glass formation, thermal stability and crystallization

Centimeter-sized Ti-based Bulk Metallic Glass with High Specific Strength

Formation and mechanical properties of bulk Cu-Ti-Zr-Ni metallic glasses with high glass forming ability

A Ti–Zr–Be–Fe–Cu Bulk Metallic Glass with Superior Glass-Forming Ability and High Specific Strength

Composition design and mechanical properties of ternary Cu–Zr–Ti bulk metallic glasses

Failure behavior of Cu–Ti–Zr-based bulk metallic glass alloys

Effect of Ti addition on mechanical properties of Zr-based bulk metallic glasses

A Ti-based bulk glassy alloy with high strength and good glass forming ability

Effects of Zr addition on the microstructures, mechanical properties and thermal stability of Cu-Ta alloys