Abstract:A glassy phase with glass transition (GT) was formed in a wide B content range of 12‒31 at% for (Co 0.75 Cr 0.125 Mo 0.125 ) 100-x B x alloys. The appearance of GT at the low metalloid content of 12%B among Co-, Fe- and Ni-based alloys is the first, in contrast to the absence of GT for (Fe 0.75 Cr 0.125 Mo 0.125 ) 88 B 12 and (Ni 0.75 Cr 0.125 Mo 0.125 ) 88 B 12 alloys. The Co-based 12%B glassy alloy crystallized through unique three stages, i.e., glass (G) → [G + hcp + fcc] → [G + fcc] → [fcc + M 23 B 6 ]. The appearance of GT is due to the necessity of long-range rearrangement of constituent elements for the simultaneous precipitation of hcp and fcc phases from glassy phase. The glass transition temperature, crystallization temperature, Vickers hardness (Hv) and Young's modulus for the Co-based glassy alloys increase linearly with increasing B content and reach 904 K, 946 K, 1566 and 188 GPa, respectively, at 31%B. The good bending plasticity is retained up to 29%B. The crystallization of the 27‒29%B alloy occurs through G → [G + M 23 B 6 ] → [M 23 B 6 + M 2 B] and the ultrahigh Hv above 2000 is attained for the metastable [G + M 23 B 6 ] phase state. The glassy alloy rod with a diameter of 1 mm was prepared for the 27%B alloy and exhibited ultrahigh yield strength of 4700 MPa, plastic strain of 1% and high oxidation resistance up to about 1200 K. The Co-based bulk glassy alloy with simultaneously high strength, ultrahigh hardness and high oxidation resistance, is promising for the future high hardness and heat-resistance materials.

Ultra-high strength Co–Ta–B bulk metallic glasses: Glass formation, thermal stability and crystallization

Ternary Co-W-B bulk metallic glasses with ultrahigh strength

Formation and ultrahigh mechanical strength of multicomponent Co-based bulk glassy alloys

Formation of Ni–Nb–Zr–X (X = Ti, Ta, Fe, Cu, Co) Bulk Metallic Glasses

Effects of Small Amount Ta on the Characteristics of the Zr-Al-Ni-Cu-Ta Bulk Metallic Glass

OsCo-based high-temperature bulk metallic glasses with robust mechanical properties

Thermal Stability and Mechanical Properties of Bulk Glassy Cu-Zr-Ti-(Nb, Ta) Alloys

Preparation and properties of new non-magnetic Co-based bulk metallic glasses

Ductile Co-based Bulk Metallic Glass with Superhigh Strength and Excellent Soft Magnetic Properties Induced by Modulation of Structural Heterogeneity

A Ti–Zr–Be–Fe–Cu Bulk Metallic Glass with Superior Glass-Forming Ability and High Specific Strength

Ternary Fe–W–B bulk metallic glasses with ultrahigh thermal stabilities

High-temperature Mo-based bulk metallic glasses

The Novel Ti-based Metallic Glass with Excellent Glass Forming Ability and an Elastic Constant Dependent Glass Forming Criterion

New Ternary Ni–Ta–Sn Bulk Metallic Glasses

Novel Soft Magnetic Co-Based Ternary Co–Er–B Bulk Metallic Glasses

Preparation and Crystallization of Ti53Cu27Ni12Zr3Al7Si3B1 Bulk Metallic Glass with Wide Supercooled Liquid Region

Fe–Y–M–B (M = Nb or Ta) Bulk Metallic Glasses with Ultrahigh Strength and Good Soft Magnetic Properties

High-temperature malleable Ta-Co metallic glass developed by combinatorial method

La-based bulk metallic glasses with critical diameter up to 30mm

Refractory Mo–Si-based Glassy Alloy Designed for Ultrahigh Strength and Thermal Stability

Synthesis,structure and Mechanical Properties of Zr-Cu-based Bulk Metallic Glass Composites