Abstract:In this work, a series of new Ni 76-x Co x Nb 4 P 16 B 4 (x = 5, 10, 15, in at.%) bulk metallic glasses (BMGs) with the maximum diameter in the range of 1.2–1.6 mm were prepared by combining fluxing and J-quenching technology. The effects of Co content on glass forming ability (GFA), thermal stability, mechanical properties, serrated-flow behaviors and corrosion performance of the present Ni-based BMGs were systematically investigated. The ranges of T g and ΔTx are 664–668 K and 21–31 K, respectively. Uniaxial compressive tests revealed that the present Ni-based BMGs have the compressive plastic strain ( εp ), yield strength ( δ y ), and fracture strength ( δ f ) that range from 16% to 27%, 2.1–2.6 GPa, and 2.2–3.6 GPa, respectively. The unprecedented mechanical properties originate from more icosahedral-like clusters (ILCs) and crystal-like clusters (CLCs) in the present Ni-based BMGs. It is found that the serrated-flow behaviors of the present Ni-based BMGs transition self-organized critical state (SOCs) into chaotic state (Cs) as plasticity decreases. The stick-slip dynamics were used to calculate the average shear-band velocity (ASBV), which shows an increasing trend as the Co content rises from 5 at.% to 15 at.%. Electrochemical measurements in 3.5 wt.% NaCl solution showed that the Ni 71 Co 5 Nb 4 P 16 B 4 BMG has a self-corrosion current density of 3.30 × 10 −8 A/cm 2 and significantly stronger corrosion resistance than austenite 316L and 304L stainless steel. The present Ni-based BMGs have excellent comprehensive performance, which has great potential for industrial applications.

New Ternary Ni–Ta–Sn Bulk Metallic Glasses

Ternary Sm–Al–Ni Bulk Metallic Glasses

Sm-based Sm-Al-Ni ternary bulk metallic glasses

Formation of Ni–Nb–Zr–X (X = Ti, Ta, Fe, Cu, Co) Bulk Metallic Glasses

Ductile Ni-based bulk metallic glasses at room temperature

Catching the Ni-based Ternary Metallic Glasses with Critical Diameter Up to 3 Mm in Ni–Nb–Zr System

Fe–Y–M–B (M = Nb or Ta) Bulk Metallic Glasses with Ultrahigh Strength and Good Soft Magnetic Properties

Quaternary Ti–Zr–Be–Ni Bulk Metallic Glasses with Large Glass-Forming Ability

Preparation of (ti0.45cu0.378zr0.10ni0.072)100−xsnx Bulk Metallic Glasses

Preparation and properties of new non-magnetic Co-based bulk metallic glasses

Ultra-high strength Co–Ta–B bulk metallic glasses: Glass formation, thermal stability and crystallization

Effects of Small Amount Ta on the Characteristics of the Zr-Al-Ni-Cu-Ta Bulk Metallic Glass

Glass forming ability, thermodynamics and mechanical properties of novel Ti–Cu–Ni–Zr–Hf bulk metallic glasses

La-based bulk metallic glasses with critical diameter up to 30mm

The Novel Ti-based Metallic Glass with Excellent Glass Forming Ability and an Elastic Constant Dependent Glass Forming Criterion

Formation and Corrosion Properties of Fe-based Bulk Metallic Glasses

A Senary TiZrHfCuNiBe High Entropy Bulk Metallic Glass with Large Glass-Forming Ability

[Ni-Mo-Si]:Nb Bulk Metallic Glasses: Microstructure, Mechanical and Corrosion Studies

A Centimeter-Sized Quaternary Ti-Zr-Be-Ag Bulk Metallic Glass

High entropy Ti20Zr20Cu20Ni 20Be20 bulk metallic glass

Formation, Thermal Stability and Mechanical Properties of Zr-Nb-Cu-Ni-Al Bulk Metallic Glasses