Abstract:In this work, a series of new Ni 76-x Co x Nb 4 P 16 B 4 (x = 5, 10, 15, in at.%) bulk metallic glasses (BMGs) with the maximum diameter in the range of 1.2–1.6 mm were prepared by combining fluxing and J-quenching technology. The effects of Co content on glass forming ability (GFA), thermal stability, mechanical properties, serrated-flow behaviors and corrosion performance of the present Ni-based BMGs were systematically investigated. The ranges of T g and ΔTx are 664–668 K and 21–31 K, respectively. Uniaxial compressive tests revealed that the present Ni-based BMGs have the compressive plastic strain ( εp ), yield strength ( δ y ), and fracture strength ( δ f ) that range from 16% to 27%, 2.1–2.6 GPa, and 2.2–3.6 GPa, respectively. The unprecedented mechanical properties originate from more icosahedral-like clusters (ILCs) and crystal-like clusters (CLCs) in the present Ni-based BMGs. It is found that the serrated-flow behaviors of the present Ni-based BMGs transition self-organized critical state (SOCs) into chaotic state (Cs) as plasticity decreases. The stick-slip dynamics were used to calculate the average shear-band velocity (ASBV), which shows an increasing trend as the Co content rises from 5 at.% to 15 at.%. Electrochemical measurements in 3.5 wt.% NaCl solution showed that the Ni 71 Co 5 Nb 4 P 16 B 4 BMG has a self-corrosion current density of 3.30 × 10 −8 A/cm 2 and significantly stronger corrosion resistance than austenite 316L and 304L stainless steel. The present Ni-based BMGs have excellent comprehensive performance, which has great potential for industrial applications.

Catching the Ni-based Ternary Metallic Glasses with Critical Diameter Up to 3 Mm in Ni–Nb–Zr System

Ni-Free Zr-Based Bulk Metallic Glasses with Critical Diameter above 20 Mm

Glass forming ability, thermodynamics and mechanical properties of novel Ti–Cu–Ni–Zr–Hf bulk metallic glasses

Formation, Thermal Stability and Mechanical Properties of Zr-Nb-Cu-Ni-Al Bulk Metallic Glasses

Effects of adding niobium on microstructures and mechanical properties of ((Zr40Ti40Ni20)72Be28)100-Nb bulk metallic glasses

Quaternary Ti–Zr–Be–Ni Bulk Metallic Glasses with Large Glass-Forming Ability

Formation of Ni–Nb–Zr–X (X = Ti, Ta, Fe, Cu, Co) Bulk Metallic Glasses

New Ternary Ni–Ta–Sn Bulk Metallic Glasses

Catching Fe-based Bulk Metallic Glass with Combination of High Glass Forming Ability, Ultrahigh Strength and Good Plasticity in Fe–Co–Nb–B System

Centimeter‐Sized Quaternary Ti‐Based Bulk Metallic Glasses with High Ti Content of 50 At%

Composition design and mechanical properties of ternary Cu–Zr–Ti bulk metallic glasses

New Centimeter-Sized Quaternary Ti–Zr–Be–Cu Bulk Metallic Glasses with Large Glass Forming Ability

A Ti–Zr–Be–Fe–Cu Bulk Metallic Glass with Superior Glass-Forming Ability and High Specific Strength

Deformation behavior, corrosion resistance, and cytotoxicity of Ni-free Zr-based bulk metallic glasses

Ductile Ni-based bulk metallic glasses at room temperature

A Centimeter-Sized Quaternary Ti-Zr-Be-Ag Bulk Metallic Glass

A Senary TiZrHfCuNiBe High Entropy Bulk Metallic Glass with Large Glass-Forming Ability

Glass-Forming Ability, Mechanical Properties, and Energetic Characteristics of ZrCuNiAlNbHfY Bulk Metallic Glasses

The Novel Ti-based Metallic Glass with Excellent Glass Forming Ability and an Elastic Constant Dependent Glass Forming Criterion

Zr–(Cu,Ag)–Al Bulk Metallic Glasses

Biocompatibility of Ni-free Zr-based Bulk Metallic Glasses