Abstract:In this work, a series of new Ni 76-x Co x Nb 4 P 16 B 4 (x = 5, 10, 15, in at.%) bulk metallic glasses (BMGs) with the maximum diameter in the range of 1.2–1.6 mm were prepared by combining fluxing and J-quenching technology. The effects of Co content on glass forming ability (GFA), thermal stability, mechanical properties, serrated-flow behaviors and corrosion performance of the present Ni-based BMGs were systematically investigated. The ranges of T g and ΔTx are 664–668 K and 21–31 K, respectively. Uniaxial compressive tests revealed that the present Ni-based BMGs have the compressive plastic strain ( εp ), yield strength ( δ y ), and fracture strength ( δ f ) that range from 16% to 27%, 2.1–2.6 GPa, and 2.2–3.6 GPa, respectively. The unprecedented mechanical properties originate from more icosahedral-like clusters (ILCs) and crystal-like clusters (CLCs) in the present Ni-based BMGs. It is found that the serrated-flow behaviors of the present Ni-based BMGs transition self-organized critical state (SOCs) into chaotic state (Cs) as plasticity decreases. The stick-slip dynamics were used to calculate the average shear-band velocity (ASBV), which shows an increasing trend as the Co content rises from 5 at.% to 15 at.%. Electrochemical measurements in 3.5 wt.% NaCl solution showed that the Ni 71 Co 5 Nb 4 P 16 B 4 BMG has a self-corrosion current density of 3.30 × 10 −8 A/cm 2 and significantly stronger corrosion resistance than austenite 316L and 304L stainless steel. The present Ni-based BMGs have excellent comprehensive performance, which has great potential for industrial applications.

Effects of adding niobium on microstructures and mechanical properties of ((Zr40Ti40Ni20)72Be28)100-Nb bulk metallic glasses

The effect of Nb addition on mechanical properties, corrosion behavior, and metal-ion release of ZrAlCuNi bulk metallic glasses in artificial body fluid

Formation, Thermal Stability and Mechanical Properties of Zr-Nb-Cu-Ni-Al Bulk Metallic Glasses

Tuning Glass Formation and Mechanical Properties of ZrCoAl(Nb) Bulk Metallic Glass with Nb Microalloying Process

Effects of Nb Addition on Icosahedral Quasicrystalline Phase Formation and Glass-Forming Ability of Zr–Ni–Cu–Al Metallic Glasses

Glass-Forming Ability, Mechanical Properties, and Energetic Characteristics of ZrCuNiAlNbHfY Bulk Metallic Glasses

Quaternary Ti–Zr–Be–Ni Bulk Metallic Glasses with Large Glass-Forming Ability

Glass Forming Ability and Mechanical Properties of New Ni-Based Bulk Metallic Glasses

[Ni-Mo-Si]:Nb Bulk Metallic Glasses: Microstructure, Mechanical and Corrosion Studies

Effect of Nb Addition on the Glass-Forming Ability, Soft-Magnetic Properties and Mechanical Properties of CoFeNiBSiNb Bulk Glassy Alloys

Effect of Nb in (La0.5ce0.5)(64-X)al16ni5cu15nbx (X=0-5) Bulk Metallic Glasses

Catching the Ni-based Ternary Metallic Glasses with Critical Diameter Up to 3 Mm in Ni–Nb–Zr System

Formation of Ni–Nb–Zr–X (X = Ti, Ta, Fe, Cu, Co) Bulk Metallic Glasses

Effect of Ti addition on mechanical properties of Zr-based bulk metallic glasses

Deformation behavior, corrosion resistance, and cytotoxicity of Ni-free Zr-based bulk metallic glasses

Corrosion behavior, mechanical properties and cell cytotoxity of Zr-based bulk metallic glasses

Ductile Ni-based bulk metallic glasses at room temperature

The effect of minor alloying on the glass forming ability and crystallization reaction of Ti32.8Zr30.2Cu9M5.3Be22.7 (M=Fe, Co, and Ni) bulk metallic glass

A CuZr-based Bulk Metallic Glass Composite with Excellent Mechanical Properties by Optimizing Microstructure

Investigation of Deformation Behavior of Zr-Ti-Ni-Cu-Be Bulk Metallic Glass Containing Nanocrystals

Improving the Glass Forming Ability and Plasticity of Zrcunialti Metallic Glass by Substituting Zr with Sc