Abstract:The effect of composition tuning on glass forming ability (GFA), mechanical properties and atomic structure in ZrxCo84−xAl16 bulk metallic glasses (BMGs) with x = 51–58 has been investigated by using copper-mold suction casting, nanoindentation, high-energy X-ray diffraction, extended X-ray absorption fine structure experiments and ab initio molecular dynamics simulations, respectively. It is found that GFA firstly increases then decreases with increasing Zr content, exhibiting a maximum diameter of 7 mm with the Zr content of 55 and 56, while an abrupt reduction of bending plasticity occurs as the Zr content drops below 55. Both experimental and theoretical results find that GFA is remarkably enhanced, due to the abnormal reduction in the fractions of the Co-centered ⟨0, 2, 8, 1⟩, ⟨0, 3, 6, 2⟩ and ⟨0, 3, 6, 3⟩ polyhedra, and the denser atomic packing of Zr atoms around center Co atom, as the Zr content increases from 51 to 56. Meanwhile, the simultaneously improved plasticity is associated with the increased Co-centered ⟨0, 3, 6, 0⟩, and Al-centered ⟨0, 2, 8, 1⟩ and ⟨0, 3, 6, 2⟩ polyhedra, which provide more fertile sites for the nucleation of shear transformations. Further Zr addition to 58 increases remarkably the fractions of Zr- and Al-centered ⟨0, 1, 10, 2⟩ and ⟨0, 3, 6, 4⟩ polyhedra, and causes looser atomic packing of Co atoms around center Zr atom, leading to the reduction in GFA. However, the plasticity is not enhanced further but remains nearly constant, which may be related to the deteriorated effect on plasticity of the decreased fractions of Zr-centered ⟨0, 1, 10, 5⟩ and Co-centered ⟨0, 3, 6, 0⟩ polyhedra, and the increased fractions of Zr-centered ⟨0, 1, 10, 3⟩ and ⟨0, 2, 8, 4⟩ and Co-centered ⟨0, 2, 8, 0⟩ polyhedra. Compositional tuning, with internal structure tuned to favor both GFA and plastic flow, offers new possibilities in developing ductile BMG materials.

Enhancement of Plasticity in Zr-based Bulk Metallic Glasses

Crystallization-aided extraordinary plastic deformation in nanolayered crystalline Cu/amorphous Cu-Zr micropillars

Substantially enhanced plasticity of bulk metallic glasses by densifying local atomic packing

Enhanced Plasticity in a Zr-based Bulk Metallic Glass Containing Nanocrystalline Precipitates

Improve plasticity of Zr-based metallic glass by surface treatment

Enhanced mechanical properties of Zr65Cu15Ni10Al10 bulk metallic glass by simultaneously introducing surface grooves and multiple shear bands

Glass forming ability and bending plasticity evolutions in Zr-Co-Al bulk metallic glasses and their structural origin

Enhanced Plasticity in Zr–Cu–Ag–Al–Be Bulk Metallic Glasses

Enhancing strength and plasticity of Zr-based bulk metallic glasses by Zr partially substituted Fe and isothermal annealing

A Plastic Zr–Cu–Ag–Al Bulk Metallic Glass

Plasticity and microstructure of Zr–Cu–Al bulk metallic glasses

Improved Tensile Ductility by Severe Plastic Deformation for Nano-Structured Metallic Glass.

Improving plasticity of the Zr46Cu46Al8 bulk metallic glass via thermal rejuvenation

Deformation behavior of Zr-based bulk nanocrystalline amorphous alloys

Improving the Glass Forming Ability and Plasticity of Zrcunialti Metallic Glass by Substituting Zr with Sc

Relation Between Icosahedral Short-Range Ordering and Plastic Deformation in Zr–Nb–Cu–Ni–Al Bulk Metallic Glasses

Mechanical Properties of Monolithic Zr62Al8Ni13Cu17 Bulk Metallic Glass

Hierarchical micro-nanostructured Zr-based metallic glass with tensile plasticity

Incorporation of ultrafine nanograins in Zr–Cu–Al–Ni–Co bulk metallic glass enabling significantly improved mechanical properties

Deformation-induced microstructural heterogeneity and rejuvenation in a Zr-based bulk metallic glass

New Class of Plastic Bulk Metallic Glass.