Abstract:Zr50Cu34-xFexAl8Ag8 (x = 0, 2, 4, 6, and 8) alloy bars of different diameters were prepared by copper mold suction casting and copper mold casting. The compressive mechanical properties of metallic glass samples with different Fe contents were determined by a universal testing machine. The microstructure and thermodynamics of the alloy samples were analyzed by X-ray diffraction, scanning electron microscopy, transmission electron microscopy, and differential scanning calorimetry. According to the experimental results, Fe doping had a significant effect on the glass-forming ability, stability, and mechanical properties of these metallic glasses. The maximum diameter of the Zr50Cu32Fe2Al8Ag8 metallic glass bar was 15 mm, and the cooling rate of the alloy sample was 7.7 K/s. The addition of Fe inhibited the formation of stable crystalline phases inside the alloy sample and improved the glass-forming ability of the metallic glass. With the addition of Fe, the DSC curve of the alloy sample moved to higher temperatures, and the characteristic temperatures and the stability of the metallic glass increased. The fracture strength (σmax) and ultimate strain (εf) of the metallic glass samples reached their maximum values of 1917.6 MPa and 3.97 %, respectively, for Zr50Cu30Fe4Al8Ag8. Compared with the Fe-free Zr50Cu34Al8Ag8 metallic glass, σmax and εf increased by 51.4 MPa and 1.19 %, respectively. With the addition of Fe, the change in the distribution and content of free volume inside the metallic glass sample is the main reason for the improvement of its mechanical properties. This study shows that trace element doping has an important effect on the properties of metallic glasses.

Effect of Sn on Plastic Deformation Ability of Fe–Si–B–P–Sn bulk Metallic Glasses

Atomic-scale Heterogeneity in Large-Plasticity Cu-doped Metallic Glasses

A Plastic FeNi-based Bulk Metallic Glass and Its Deformation Behavior

Effects of Cu Additions on Mechanical and Soft-Magnetic Properties of CoFeBSiNb Bulk Metallic Glasses

Fe-Based Bulk Metallic Glass with High Plasticity

Effect of Fe addition on the glass-forming ability, stability, and mechanical properties of Zr50Cu34-xFexAl8Ag8 metallic glasses

Effects of Ni Substitution for Fe/Co on Mechanical and Magnetic Properties of Co-based Bulk Metallic Glasses

A New Ti–Zr–Hf–Cu–Ni–Si–Sn Bulk Amorphous Alloy with High Glass-Forming Ability

Correlation Between Deformation Behavior and Atomic-Scale Heterogeneity in Fe-based Bulk Metallic Glasses

Effect of Sn on Glass Formation Ability and Crystallization Behaviors of Cu-Based Bulk Metallic Glass Alloy

Superductile Bulk Metallic Glass

Deformation-enhanced hierarchical multiscale structure heterogeneity in a Pd-Si bulk metallic glass

Can Severe Plastic Deformation Tune Nanocrystallization in Fe-Based Metallic Glasses?

Enhancing the tribological performance of the TiZrHfCuBe high entropy bulk metallic glass by Sn addition

Co Content Effect on Elastic Strain Limit in ZrCuNiAlCo Bulk Metallic Glasses

Magnetic Properties and Glass-Forming Ability of Modified Fe–P–Si–B Bulk Amorphous Alloys

Substantially enhanced plasticity of bulk metallic glasses by densifying local atomic packing

Effects of Ni and Si Additions on Mechanical Properties and Serrated Flow Behavior in FeMoPCB Bulk Metallic Glasses

The Effect of Co Addition on Glassy Forming Ability and Soft Magnetic Properties of Fe-Si-B-P Bulk Metallic Glass

Influence of minor Si addition on the glass-forming ability and mechanical properties of Pd40Ni40P20 alloy

Densification and heterogeneity enhancement of Fe-based metallic glass under local plastic flow