Abstract:AlN-SiC solid solution particles with a variety of morphologies including faceted polyhedrons with or without ledges; hexagonal platelets; hexagonal columns with a hexagonal plate or a pyramidal cap; and interpenetrating cones, have been found in the combustion products of a mixture of Al, Si, and carbon black under a nitrogen pressure of 10 MPa. Combustion temperature (the growth temperature of crystals) is the most important factor controlling the morphology of crystals formed in the combustion product. When temperatures are close to the melting point of the solid solutions, a small driving force for nucleation and long distances of surface migration make nucleation on the basal plane difficult, and thus the solid solution particles tend to grow as platelets. Supersaturation is the second key factor influencing crystal growth. At relatively low temperatures, a low supersaturation at the large pores renders nucleation difficult and the solid solution particles tend to grow as platelets. At relatively low temperatures and high supersaturation, a relatively high driving force for nucleation and short mean distances of surface migration promote the growth of AlN-SiC solid solutions as polyhedrons. The formation of the ledges on the polyhedral particles is attributed to the differences in the evaporation rates and the deposition rates between Al and Si. At relatively low temperatures and an intermediate supersaturation, the solid solution particles grow as prismatic columns. The formation of the prismatic columns with a hexagonal plate, or a pyramidal cap, is attributed to a sudden change of temperature during combustion. A possible growth mechanism for the AlN-SiC solid solution cones is proposed.

Effect of Additives on Self-Propagating High-Temperature Synthesis of Aln

Highly Crystalline Aln Particles Synthesized by Shs Method

Morphology-Controlled Synthesis of Quasi-Aligned Aln Nanowhiskers by Combustion Method: Effect of Nh4cl Additive

Effect of a NiO Additive on Interaction in a Ni–Al–W System in Self-Propagating High-Temperature Synthesis

Effect of Nitrogen Pressure and Oxygen-Containing Impurities on Self-Propagating High Temperature Synthesis of Si3n4

Combustion synthesis of fine aluminum nitride powders under micropositive N 2 pressure with water additive

Growth of flower-like AlN by combustion synthesis assisted with mechanical activation

Thermodynamics and Kinetic Considerations behind the Growth of AlN Whiskers Synthesized by Carbothermal Reduction

Gas-Phase Chemical Reaction Mechanism in the Growth of AlN during High-Temperature MOCVD: A Thermodynamic Study

Effects of NH4Cl on the synthesis of aluminum nitride by the spontaneous combustion of mechanically activated aluminium powder

Effect of Additive Sm2O3 on Synthesizing AlN Ceramics at High Pressure

Mechanism and Kinetics Analysis of AlN Combustion Synthesis

Combustion Synthesis of Rod-Like AlN Nanoparticles

Combustion Synthesis of AlN Whiskers

Growth Mechanisms for SiC-AlN Solid Solution Crystals Prepared by Combustion Synthesis

Self-propagating high-temperature synthesis of AlN in a graphite crucible in air by mechanical activation

AlN Powder Synthesis by Sodium Fluoride-Assisted Carbothermal Combustion

Synthesis of AlN nanocrystalline powders

Facile solvent-free synthesis of pure-phased AlN nanowhiskers at a low temperature

Investigation On Combustion Synthesis Of Aln Whisker

Promoting Effect of Silicon Particles on Gas-Diffusion-reaction System: In-situ Synthesis of AlN in Al-Si Materials