Abstract:Using Mo, Si, and C element powders as starting materials, a field-activated and pressure-assisted combustion synthesis (FAPACS) was employed to synthesize high-density bulk MoSi2–SiC composite in one step. Effects of sintering temperatures (1100, 1200, 1400 and 1600°C) on microstructures and densification were investigated. With the exception of 1100°C, at which synthesis was incomplete, the FAPACS was characterized by the four stages, i.e. initial expansion, slight shrinkage, abrupt shrinkage and slight expansion. The study shows that the sintering ability at the higher temperature is better than that at the relatively lower temperature. When the sintering temperature reaches 1400 or 1600°C with holding time of 10min, the high-temperature transitional phases, i.e. Mo4.8Si3C0.6, were presented and the produced SiC particles are agglomerate. The relative density of the products (holding time: 10min) was improved tremendously from 59% to 96.0% over the range 1100–1400°C, and a smaller enhancement in densification up to 98.5% was achieved between 1400 and 1600°C. Moreover, an extended holding time (up to 20min) at 1600°C resulted in nearly Mo4.8Si3C0.6-free and dense MoSi2–SiC products with the relative density of 99.0%. Simultaneously, a locally uniform distribution of SiC in the synthesized MoSi2 matrix was achieved. And the interfaces between the synthesized phases are clean without impurities (e.g. SiO2) and porosities. Thereby, in order to pursue an equilibrium among densification, microstructural uniformity and formation of transitional phases, the most suitable sintering temperature and holding time for fabrication of MoSi2–SiC by FAPACS are recommended to be 1600°C and 20min in the present work.

Synthesis of Mosi2/Wsi2 Nanocrystalline Powder by Mechanical-Assistant Combustion Synthesis Method

Synthesis of Mosi2 by Mechanical Alloying

Synthesis and analysis of high-purity MoSi2 powder

Preparation and properties of W-Mo-Cu composite using solution combustion synthesized W Mo solid solution nanopowder

Synthesis of nanocrystalline cubic substoichiometric WC1 − z powders by mechanochemical technology

Combustion Synthesis of Nanosized Β-Sic Powder on a Large Scale

Synthesis of Mo(Si, Al)2 Powders by Mechanical Alloying

Mechanosynthesis Mechanism of Tic Powders

Combustion synthesis of SiC/Al2O3 composite powders with SiC nanowires and their growth mechanism

Nanomaterials Via Solution Combustion Synthesis: a Step Nearer to Controllability

Studies of synthesizing the SiC nanometer powders by chemical vapor reaction

Preparation of Ti/Al based nanophase composite powder by mechanical alloying

On the Progress of Combustion Synthesis of Si3n4 Ceramic: from Laboratory Research to Industrial Production

Microstructures and densification of MoSi2–SiC composite by field-activated and pressure-assisted combustion synthesis

Preparation of Intermetallic Compound MoSi2 by Mechanical Alloying Method

Synthesis of SiC/MoSi2 composite by mechanical alloying and reactive sintering

On the Progress of Combustion Synthesis of Si<sub>3</sub>N<sub>4</sub> Ceramic: From Laboratory Research to Industrial Production

Synthesis of nanocrystalline silicon carbide powders

Synthesis of SiO2 covered SiC nanowires with milled Si,C nanopowders

Thermodynamic Calculation and an Experimental Study of the Combustion Synthesis of (mo1−nb )si2 (0 ⩽x⩽ 1)

Combustion synthesis of α-Si3N4 powders using in-situ nano-SiO2 coated Si and Si3N4 reactants