Synthesis of Mo(Si, Al)2 Powders by Mechanical Alloying

XIAO Lai-rong,YI Dan-qing,Song Cheng,CAI Zhi-gang,XU Liang-liang

DOI: https://doi.org/10.3969/j.issn.1673-0224.2005.02.006

2005-01-01

Abstract:Mo(Si 1-x , Al x) 2 powders have been synthesized by means of mechanical alloying with MoSi 2, Mo and Al mixture powders. The phase change and grain size of powders were characterized by X-ray diffraction. The appearance and particle size of powders were determined by SEM. Using Burgio model, the synthesis energy of Mo(Si, Al) 2 by mechanical alloying was calculated. Results show that there are MoSi 2 and Mo(Si, Al) 2 after milled for 5h, no remained pure powders and no Al-Mo interim phase appearing in the milling process of MoSi 2, Mo and Al mixture powders; the particle size is nearly sub-micro after milled for 40h and the grain size is 21~40nm. The formation mechanism of Mo(Si, Al) 2 by mechanical alloying is similar self-propagation high-temperature synthesis(SHS), and the milling energy of about 15.4kJ/g will be needed for the phase formation.