An Xps Study on the Degradation of Lead Magnesium Niobate-Based Relaxor Ferroelectrics During Nickel Electroplating

JL Cao,LT Li,ZL Gui
DOI: https://doi.org/10.1039/b006953l
2001-01-01
Journal of Materials Chemistry
Abstract:Resistance degradation of Pb(Mg1/3Nb2/3)O-3-Pb(Zn1/3Nb2/3)O-3-PbTiO3 (PMZNT) relaxor ferroelectrics during nickel electroplating was investigated by resistivity measurement and X-ray photoelectron spectroscopy (XPS) through the appearance of changes in Nb 3d and Pb 4f spectra. It was found that the insulation resistance of the PMN-based ceramics decreased after electroplating. The XPS analysis showed that the ceramic materials had been reduced by hydrogen during electroplating and Nb4+ and metallic Pb were generated. As a result, oxygen vacancies and free electrons were created and, therefore, increased the conductivity of the ferroelectrics. It was also found that Nb5+ reduction was prior to Pb2+ reduction. On the basis of our experiments, two conduction mechanisms involved in the hydrogen-induced resistance degradation were established.
What problem does this paper attempt to address?