Abstract:Resistance degradation of lead magnesium niobate (PMN)-based relaxor ferroelectrics during nickel electroplating, as well as the recovery of the degraded specimen through air annealing, were investigated by using resistance measurement and X-ray photoelectron spectroscopy (XPS). It was found that the resistivity of the ceramics declined nonlinearly with the electroplating time, and eventually, an obvious degradation occurred. The XPS results showed that parts of Pb2+ and Nb5+ were reduced to metallic Pb and Nb4+ by hydrogen during electroplating. In view of defect chemistry, oxygen vacancies and free electrons were produced, leading to the resistance degradation. It was also found that the degraded PMN-based ceramics could regain its resistivity characteristics after being annealed in air at high temperatures. The correlation of Pb and Nb4+ reoxidation and the resistivity recovery was clarified, which in turn confirmed that the generation of metallic Pb and Nb4+ resulted in the resistance degradation of the ceramics during nickel electroplating. (C) 2001 The Electrochemical Society.

Resistance Degradation Of Lead Magnesium Niobate-Based Ceramics During Nickel Electroplating And Recovery Through Air Annealing